Polymer Property : Tensile Strength, Ultimate = 2440 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 16.8 MPa
2440 psi
ASTM D638-95
Multibase Multi-Flex® TPO D-6507
Multi-Flex® D 6507 is a mineral filled TPO polypropylene compound designed for applications requiring high impact and moderate stiffness.Data provided by Multibase.
Tensile Strength, Ultimate 16.8 MPa
2440 psi
ASTM D638
Multibase Multi-Pro® 2520 XU Black Polypropylene
Forms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase
Tensile Strength, Ultimate 16.8 MPa
2440 psi
ASTM D412-80
DuPont Performance Polymers Hypalon® 48 Chlorosulfonated Polyethylene Rubber, Mineral Filled Compound  (discon
Mineral filled compound with 100 parts Hypalon; 80 parts hard clay; 4 parts magnesia; 30 parts aromatic process oil; 3 parts pentaerythritol; and 2 parts Tetrone® A rubber accelerator (from DuPont ..
Tensile Strength, Ultimate 16.8 MPa
2440 psi
The Chemical Company ChemFlexx™ 206 Phthalate Plasticizer
Chemflexx 206 is considered to be a “functional replacement” for linear plasticizers. It is an organic, non-hazardous, liquid, phthalate ester. Chemflexx 206 is a plasticizer for the manufacture ..
Tensile Strength, Ultimate 16.8 MPa
2440 psi
oven aged 10 days @ 100°C
The Chemical Company ChemFlexx™ 206 Phthalate Plasticizer
Chemflexx 206 is considered to be a “functional replacement” for linear plasticizers. It is an organic, non-hazardous, liquid, phthalate ester. Chemflexx 206 is a plasticizer for the manufacture ..
Tensile Strength, Ultimate 16.8 MPa
2440 psi
Dow Primacor® 2912 Ethylene Acrylic Acid (EAA)
PRIMACOR® 2912 polymer containing 9.5% comonomer is an extrusion/ coextrusion coating resin for flexible packaging applications. It is designed to provide excellent adhesion to metallic, paper and ..
Tensile Strength, Ultimate 16.8 MPa
2440 psi
Die C (35 min / 145°C); ASTM D412
Dow SE BR-1203H Stereospecific high cis-1,4 Polybutadiene (BR)
SE BR-1203H is manufactured by a solution process using cobalt catalyst which produces polymers with a very light color and low ash content. A non-staining stabilizer is added during the production..