Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | ASTM D638 |
NCMT NanoPAC™ HS403 High Performance Polypropylene Nanocomposite Applications: Electrical AppliancesInformation provided by Nano Composite Materials Technology Limited |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | ASTM D638 |
NCMT NanoPAC™ HS404 High Performance Polypropylene Nanocomposite Applications: Electrical AppliancesInformation provided by Nano Composite Materials Technology Limited |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | ASTM D638 |
NOVA Chemicals Sclair® 51-35BP HDPE Extrusion Resin Features: Medium molecular weight, excellent ESCR, excellent toughness, good processability, good chemical resistance.Applications: Extrusion on to metal pipes to produce a corrosion resistant coati.. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | |
Reliance Industries BIOMER P226 compared to PPInformation provided by Reliance Industries |
|||
Tensile Strength, Ultimate | 24.0 - 138 MPa | 3480 - 20000 psi | Average value: 40.4 MPa Grade Count:64 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded". Each property range of values reported is .. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | ASTM D638 |
Reliance Industries Relene E41003 Polyethylene Relene E41003 is a High Density Polyethylene grade with broad molecular weight distribution and good melt strength , suitable for making pipes for water supply, irrigation, sewage and industrial eff.. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | Compounded Tire |
Polynorbornene Rubber (PNR) High glass temperature - plasticizer needed to make a 'rubbery' compound. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | ASTM D638 |
IDI Composites 46-3 Thermoset Polyester, Molding Superior electrical performance with low pressure molding for V-O flammability in encapsulation applications.Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | ASTM D412 |
KKPC KOSYN KTR 201 Thermoplastic Elastomer (TPE) Thermoplastic Elastomer (TPE)Characteristics: KOSYN KTR101 is linear block copolymer made by solution polymerization which polymerizes butadiene and styrene in organic solvent. It is thermoplastics .. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | ASTM D638 |
Ineos Styrenics Avantra® 585K Q402 Rubber Modified Polystyrene Avantra® 585K Q402 is a high-impact grade of polystyrene with extremely high surface gloss and excellent practical toughness. Although Avantra® 585K Q402 can be processed by any method applic.. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | ASTM D638 |
Ineos Styrenics Avantra® 585K Rubber Modified Polystyrene Avantra® 585K is a high-impact grade of polystyrene with extremely high surface gloss and excellent practical impact strength. Although Avantra® 585K can be processed by any method applicable.. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 372 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 401 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 372 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 401 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 372 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 372 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 401 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 372 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 372 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 401 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | ASTM D638 |
Covestro Bayflex® 110-50 Polyurethane Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | ASTM D638/D412 |
Covestro Bayflex® 110-80 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System 0.125 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and o.. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | ASTM D638/D412 |
Covestro Bayflex® XGT-50 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System 0.125 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and of.. |
|||
Tensile Strength, Ultimate | 24.0 - 27.0 MPa | 3480 - 3920 psi | |
Biomer P226 PHB Biodegradable Polymer PHB is a isotactic, absolutely linear, thermoplastic homopolyester built of 3-hydroxy butyric acid. The formula of the subunit is -[O-CH(CH3)-CH2-CO]-. PHB is free from even traces of catalysts. P.. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | ASTM D638 |
Solvay Specialty Polymers Algoflon® 15GR PTFE; Graphite Filled
(discontinued **) Data provided by the manufacturer.15 wt.% Graphite. Suspension polymer powder grade recommended for compression molding. Pure PTFE possesses high inertness, excellent dielectric properties, almost n.. |
|||
Tensile Strength, Ultimate | 24.0 - 102 MPa @Strain 2.00 - 30.0 % |
3480 - 14800 psi @Strain 2.00 - 30.0 % |
Average value: 53.1 MPa Grade Count:3 |
Overview of materials for Thermoplastic Polyurethane (TPUR), Polyester Grade This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Polyurethane (TPUR), Polyester Grade". Each property range of values reported is minimum a.. |
|||
Tensile Strength, Ultimate | 24.0 - 102 MPa @Temperature 0.000 - 60.0 °C |
3480 - 14800 psi @Temperature 32.0 - 140 °F |
Average value: 53.1 MPa Grade Count:3 |
Overview of materials for Thermoplastic Polyurethane (TPUR), Polyester Grade This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Polyurethane (TPUR), Polyester Grade". Each property range of values reported is minimum a.. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | ASTM D412 |
KKPC KOSYN KTR 101 Thermoplastic Elastomer (TPE) Thermoplastic Elastomer (TPE)Characteristics: KOSYN KTR 100-800 series are linear block copolymers made by solution polymerization which polymerizes butadiene and styrene in organic solvent. It is t.. |
|||
Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | ASTM D638 |
ExxonMobil Iotek® 7310 Zinc Ionomer
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A low melt index zinc ionomer made from an ethylene acrylic acid base polymer.Applications: Injection molding; Impact modifier of polyamide. |