Polymer Property : Tensile Strength, Ultimate = 22500 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	155 MPa	22500 psi	ISO 527
Wellman Wellamid® GFT33N051-N2 33% Impact Modified Glass Reinforced Nylon 66/6, Lubricated & Heat Stabilized &n Typical Applications: Machinery gear trains and linkage, conveyor belt links, fasteners, auto under hood and door parts, automotive door handles, appliance parts, sporting goods, lawn and garden equ..
Tensile Strength, Ultimate	155 - 280 MPa	22500 - 40600 psi	Average value: 230 MPa Grade Count:13
Overview of materials for Nylon 66/6, 60% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 60% Glass Fiber Reinforced". Specific grades with glass content between 55% and 64% are incl..
Tensile Strength, Ultimate	155 MPa	22500 psi	ISO 527-1, 2
Polyplastics Duranex® 3400 Polybutylene Terephthalate (PBT), Standard, 40% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Tensile Strength, Ultimate	155 MPa	22500 psi	ACMA Test #4
CoorsTek AD-85 Alumina (nom. 85% Al2O3) Thermal Shock Delta Tc = 300°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar..
Tensile Strength, Ultimate	155 MPa	22500 psi	5mm/min; ISO 527
BASF Petra® 130 30% Glass Filled PET Petra 130 is a 30% glass fiber reinforced polyethylene terephthalate (PET) for injection molding applications. It exhibits a good combination of performance properties including high strength and s..
Tensile Strength, Ultimate	155 MPa	22500 psi	5mm/min; ISO 527
BASF Ultramid® 8233G HS BK-106 33% Glass Filled PA6 (Dry) Ultramid 8233G HS BK-106 is a heat stabilized, weather resistant, 33% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature performance and ..
Tensile Strength, Ultimate	155 MPa @Temperature 871 °C	22500 psi @Temperature 1600 °F	ASTM E8
ATI Allegheny Ludlum 310S Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo..
Tensile Strength, Ultimate	155 MPa @Temperature 871 °C	22500 psi @Temperature 1600 °F
ATI Allegheny Ludlum 316Ti Austenitic Stainless Steel Characteristics:excellent resistance to general corrosion, excellent resistance to pitting/crevice corrosion, resistant to sensitization, better creep stress-rupture and tensile strength at elevated..
Tensile Strength, Ultimate	155 MPa	22500 psi	5mm/min; ISO 527
BASF Ultramid® HMG13 HS BK-102 63% Glass Filled PA6 (Conditioned) Ultramid HMG13 HS BK-102 is a 63% glass filled, injection molding, high modulus nylon designed to have high strength and stiffness for metal replacement applications. It also has excellent moldabil..
Tensile Strength, Ultimate	155 MPa	22500 psi	Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Edgetek® PI-20GM-20CF/000 Polyetherimide (PEI), Carbon/Glass Filled (discontinued **) Description/Features:Milled Glass Fiber ReinforcedCarbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.