Polymer Property : Tensile Strength, Ultimate = 21800 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	54.5 - 150 MPa	7900 - 21800 psi	Average value: 97.2 MPa Grade Count:42
Overview of materials for Polyetheretherketone, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, Unreinforced". Each property range of values reported is minimum and maximum value..
Tensile Strength, Ultimate	62.1 - 150 MPa	9000 - 21800 psi	Average value: 102 MPa Grade Count:7
Overview of materials for Polyamide-Imide, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polyamide-Imide, Molded". Each property range of values reported is minimum and maximum values of approp..
Tensile Strength, Ultimate	27.6 - 150 MPa	4000 - 21800 psi	Average value: 84.3 MPa Grade Count:10
Overview of materials for Polyphenylene Sulfide (PPS); Molded This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS); Molded". Each property range of values reported is minimum and maximum valu..
Tensile Strength, Ultimate	140 - 150 MPa @Temperature 80.0 - 80.0 °C	20300 - 21800 psi @Temperature 176 - 176 °F	Average value: 128 MPa Grade Count:4
Overview of materials for Nylon 66/6, 40% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 40% Glass Fiber Reinforced". Specific grades with glass content between 35% and 44% are incl..
Tensile Strength, Ultimate	38.0 - 150 MPa	5510 - 21800 psi	Average value: 78.2 MPa Grade Count:87
Overview of materials for Nylon 66, Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass Bead Filled". Each property range of values reported is minimum and maximum values of ap..
Tensile Strength, Ultimate	60.0 - 150 MPa @Temperature 120 - 200 °C	8700 - 21800 psi @Temperature 248 - 392 °F	Average value: 103 MPa Grade Count:7
Overview of materials for Nylon 46, Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Glass Fiber Reinforced". Each property range of values reported is minimum and maximum values ..
Tensile Strength, Ultimate	45.0 - 150 MPa	6530 - 21800 psi	Average value: 70.5 MPa Grade Count:22
Overview of materials for Nylon 6, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, PTFE Filled". Each property range of values reported is minimum and maximum values of appropria..
Tensile Strength, Ultimate	80.0 - 150 MPa @Temperature 70.0 - 175 °C	11600 - 21800 psi @Temperature 158 - 347 °F	Average value: 104 MPa Grade Count:3
Overview of materials for Nylon 6, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. E..
Tensile Strength, Ultimate	80.0 - 150 MPa @Time 180000 - 7.20e+7 sec	11600 - 21800 psi @Time 50.0 - 20000 hour	Average value: 104 MPa Grade Count:3
Overview of materials for Nylon 6, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. E..
Tensile Strength, Ultimate	81.4 - 150 MPa	11800 - 21800 psi	Average value: 118 MPa Grade Count:23
Overview of materials for Polyethersulfone (PES), 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 20% Glass Fiber Filled". Each property range of values reported is minimum and m..
Tensile Strength, Ultimate	50.0 - 150 MPa	7250 - 21800 psi	Average value: 125 MPa Grade Count:18
Overview of materials for Polyethersulfone (PES), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% ..
Tensile Strength, Ultimate	75.0 - 150 MPa	10900 - 21800 psi	Average value: 102 MPa Grade Count:29
Overview of materials for Polyethylene Terephthalate (PET), 20% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 20% Glass Reinforced". Specific grades with glass content between 15% ..
Tensile Strength, Ultimate	60.0 - 150 MPa @Temperature 60.0 - 230 °C	8700 - 21800 psi @Temperature 140 - 446 °F	Average value: 100 MPa Grade Count:8
Overview of materials for Polyphthalamide (PPA), 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are..
Tensile Strength, Ultimate	30.0 - 150 MPa	4350 - 21800 psi	Average value: 96.4 MPa Grade Count:97
Overview of materials for Polypropylene with 40% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Glass Fiber Filler". Specific grades with glass content between 35% and 44% are i..
Tensile Strength, Ultimate	20.0 - 150 MPa	2900 - 21800 psi	Average value: 50.1 MPa Grade Count:83
Overview of materials for Polypropylene, Glass/Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Glass/Mineral Reinforced". Each property range of values reported is minimum and maximum ..