Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 135 - 145 MPa @Temperature 130 - 180 °C |
19600 - 21000 psi @Temperature 266 - 356 °F |
Average value: 107 MPa Grade Count:4 |
Overview of materials for Polyphthalamide (PPA), 50% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 50% Glass Fiber Reinforced". Each property range of values reported is minimum and maxi.. |
|||
Tensile Strength, Ultimate | 135 - 145 MPa @Time 1.80e+7 - 7.20e+7 sec |
19600 - 21000 psi @Time 5000 - 20000 hour |
Average value: 107 MPa Grade Count:4 |
Overview of materials for Polyphthalamide (PPA), 50% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 50% Glass Fiber Reinforced". Each property range of values reported is minimum and maxi.. |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | ASTM D638 |
Chevron Phillips Ryton® R-7 Polyphenylene Sulfide Compound
(discontinued **) Natural Color Polyphenylene Sulfide CompoundRyton® R-7 is polyphenylene sulfide compounded with glass fibers and mineral fibers to produce an injection moldable high temperature engineering compoun.. |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | ISO 527 |
Solvay Technyl® A 218 V30 Nylon 66, 30% Glass Fiber, EH50 Polyamide PA66, reinforced with 30% of glass fiber, heat stabilized, for injection molding.Technyl A 218 V30 is used in all sectors of industry, offering an excellent combination between thermal and.. |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | ISO 527 |
Solvay Technyl® A 216 V30 Nylon 66, 30% Glass Fiber, EH50 Polyamide PA66, reinforced with 30% of glass fiber, for injection molding.Technyl A 216 V30 is used in all sectors of industry, offering an excellent combination between thermal and mechanical prope.. |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | ISO 527 |
Wellman Wellamid® GF20-60 XE-N 20% Glass Fiber Reinforced Nylon 6, Lubricated & Heat Stabilized Typical Applications: Radio and TV components, dishwasher roller carriages, chain saw oil reservoirs, gears, housings, door & window latches, power hand tool housings, high temperature devices.Data .. |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | ISO 527-1, 2 |
Polyplastics Duranex® 750LD Polybutylene Terephthalate (PBT), Low warpage, 30% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | dry; ISO 527-1/-2 |
DSM Akulon® XG-FKGS6 PA6-GF30 FR 30% Glass Reinforced, Flame Retardant, Halogen free |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | |
Covestro Makrolon® 8345 Polycarbonate High viscosity injection molding and extrusion grade with 35% standard glass fibers and easy mold release, stiff flow, especially high strength and stiffness.Information provided by Bayer.As of 1 Se.. |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | dry; ISO 527-1/-2 |
DSM Novamid® 1010GN2-20 NAT/BK37 PA6-GF20 FR(17) 20% Glass Reinforced, Flame Retardant |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | cond; ISO 527-1/-2 |
DSM Stanyl® OCD2300 BLK PA46-GF50 50% Glass Reinforced, Heat Stabilized |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | dry; ISO 527-1/-2 |
DSM EcoPaXX® Q-KGS6 PA410-GF30 FR 30% Glass Reinforced, Flame Retardant (Halogen free) |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | 5mm/min; ISO 527 |
BASF Petra® 330 FR BK-112 30% Glass Filled PET Petra 330 FR BK-112 is a 30% glass reinforced, flame retardant PET, pigmented black injection molding compound rated UL94 V-0 in a 1/64 inch thickness. The product is designed for injection molding.. |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | 5mm/min; ISO 527 |
BASF Ultradur B 4040 G6 LS High Speed BK15029 30% Glass Filled PBT/PET |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | 5mm/min; ISO 527 |
BASF Ultradur B 4300 G6 LS BK15073 30% Glass Filled PBT mt |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | ATSM D638 |
Ashley Polymers Ashlene® 527LD-33G Nylon 66, High Impact, 33% Glass Reinforced A high impact reinforced Nylon 66 with good low temperature properties.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | 5mm/min; ISO 527 |
BASF Ultramid® N-276 NF3001 40% Glass/Mineral Filled PA66 (Dry) Ultramid N-276 NF3001 is a 40% mineral/glass reinforced, heat stabilized injection molding nylon 6/6. |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | 5mm/min; ISO 527 |
BASF Ultradur B 4300 G6 BK5110 30% Glass Filled PBT Ultradur B 4300 G6 BK5110 is an easy flowing, pigmented black, injection molding PBT with 30% glass fiber reinforcement for rigid, tough, and dimensionally stable parts. |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | 5mm/min; ISO 527 |
BASF Ultradur B 4406 G6 Q113 30% Glass Filled PBT Ultradur B4406 G6 Q113 is an UL V0 injection molding, PBT grade with 30% glass fiber reinforcement. |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | ASTM D638 |
Toyobo Vylopet® EMC120K Glass Reinforced Polyester, Easy Molding Grade Flame retardant V-0 UL-94 classApplications: Electric and electronic componentsGeneral features of Vylopet® include heat resistance, good mechanical properties, high dielectric strength and trackin.. |
|||
Tensile Strength, Ultimate | 135 MPa @Temperature 60.0 °C |
19600 psi @Temperature 140 °F |
ISO 527 |
LATI LARTON G/50 50% Glass Fiber Filled Polyphenylene sulfide (PPS)
(discontinued **) Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex.. |
|||
Tensile Strength, Ultimate | 135 MPa @Temperature 1093 °C |
19600 psi @Temperature 1999 °F |
|
Haynes 230® alloy, hot rolled and 1232°C solution annealed plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | 5mm/min; ISO 527 |
BASF Ultramid® B3GM35 Ebony23227 15/25% Glass/Mineral Filled PA6 (Dry) Ultramid B3GM35 Ebony23227 is a 40% combined glass-fiber and mineral reinforced, pigmented black injection molding PA6 grade. |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | ASTM D638 |
Solvay Specialty Polymers Xydar® G-430 Glass Filled Liquid Crystal Polymer
(discontinued **) XYDAR G-430 Liquid Crystal Polymer (LCP) is a glass reinforced injection molding grade developed specifically for electronic applications utilizing surface mount technology at lead-free solder tempe.. |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | ISO 527 |
LATI LARTON G/40 40% Glass Fiber Filled Polyphenylene sulfide (PPS)
(Unverified Data**) Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex.. |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | ISO 527 |
LATI LARAMID G/30 30% Glass Filled Polyphthalamide (PPA) Based Compound
(Unverified Data**) Laramid compounds are based on a unique semi-crystalline engineering polymer (polyphthalamide) offering improved performance compared to traditional engineering thermoplastics at a lower cost than s.. |
|||
Tensile Strength, Ultimate | 135 MPa | 19600 psi | ISO 527 |
Solvay Specialty Polymers Amodel® A-6625 HS BK324 Polyphthalamide, 25% carbon/glass fiber, ESD grade
(discont Amodel A-6625 HS BK324 is a 25% carbon and glass-fiber-reinforced, heat-stabilized grade of polyphthalamide (PPA). It is formulated for applications requiring the dissipation of static charge. This .. |