Polymer Property : Tensile Strength, Ultimate = 18.8 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	18.8 MPa	2730 psi	ASTM D412-80
DuPont Performance Polymers Hypalon® 45 Chlorosulfonated Polyethylene Rubber, Mineral Filled Compound (discon Mineral filled compound with 100 parts Hypalon; 80 parts hard clay; 4 parts magnesia; 30 parts aromatic process oil; 3 parts pentaerythritol; and 2 parts Tetrone® A rubber accelerator (from DuPont ..
Tensile Strength, Ultimate	18.8 MPa	2730 psi	Cured
KKPC KOSYN KBR 31 Polybutadiene Rubber (High cis BR) Polybutadiene Rubber (High cis BR)Characteristics: KBR 31 contains an aromatic oil additive. Polybutadiene Rubber (BR), which has three kinds of bond structure of cis-1,4, trans-1,4, vinyl, is simp..
Tensile Strength, Ultimate	18.8 MPa	2730 psi	Vulcanizate, Press cured, TC95 +3min at 160°C
Dow Nordel® IP 4520 Molded Brake Part FormulationNordel® IP 4520
Tensile Strength, Ultimate	18.8 MPa	2730 psi	Vulcanizate, Press cured, TC95 +3min at 160°C
Dow Nordel® IP 4770P General Purpose Compound FormulationNordel® IP 4770P
Tensile Strength, Ultimate	18.8 MPa	2730 psi	Vulcanizate, Press cured, TC95 +3min at 160°C
Dow Nordel® IP 4770R General Purpose Compound FormulationNordel® IP 4770R
Tensile Strength, Ultimate	18.8 - 152 MPa	2730 - 22000 psi	Average value: 42.9 MPa Grade Count:18
Overview of materials for Polypropylene, Film Grade This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Film Grade". Each property range of values reported is minimum and maximum values of appr..