Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 17.6 MPa | 2550 psi | |
Freudenberg Simrit V123 Standard Fluoroelastomer Excellent resistance to petroleum products and solvents. Very good high-temperature performance. Fluorocarbon elastomers make up the most widely used seals in the semiconductor industry. Avoid polar.. |
|||
Tensile Strength, Ultimate | 17.6 MPa | 2550 psi | |
Indium Corp. Indalloy® 2 In-Pb-Ag Solder Alloy Especially useful for soldering against gold, as leaching is minimized. Good thermal fatigue properties. Compatible with Indalloy numbers 204, 205, 206, 7, 10 and 150 in step-soldering applications... |
|||
Tensile Strength, Ultimate | 17.6 MPa | 2550 psi | |
Sylvin Technologies 8960-95 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 17.6 MPa | 2550 psi | |
Williams Advanced Alloys WS149 Solder All Williams alloys are available in a variety of shapes and forms, including ribbon, preforms, rod, ring, wire, and custom shapes.Information provided by Williams Advanced Alloys |
|||
Tensile Strength, Ultimate | 17.6 MPa | 2550 psi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
DuPont Performance Polymers VTR GLT Peroxide Cured Fluoroelastomer (FKM) Formulation FormulationViton® VTR-8500 |
|||
Tensile Strength, Ultimate | 17.6 MPa | 2550 psi | ASTM D412 |
Colorite Polymers CS8042SC Wire and Cable Jacket Vinyl Compound Description: Colorite specialty wire and cable compounds feature low smoke properties, excellent flame retardance, low temperature flexibility, and resistance to abrasion and chemicals. All are avai.. |
|||
Tensile Strength, Ultimate | 17.6 MPa | 2550 psi | |
Dow Primacor® 3440 Ethylene Acrylic Acid (EAA) PRIMACOR® 3440 polymer containing 9.5% comonomer is an extrusion/ coextrusion coating and laminating for flexible packaging applications. It is designed to provide excellent hot tack and adhesion t.. |
|||
Tensile Strength, Ultimate | 17.6 MPa | 2550 psi | |
Colorite Polymers 8011 Clear Extrusion Vinyl Compound Description: Clear non-toxic vinyl compounds are utilized by the health and medical industries for the extrusion of various components for the production of devices. The vinyl components used in pre.. |
|||
Tensile Strength, Ultimate | 17.6 MPa | 2550 psi | |
Colorite Polymers 8012 Clear Injection Molding Vinyl Compound Description: Clear non-toxic vinyl compounds are utilized by the health and medical industries for injection molding of various components such as drip chambers, connectors, valves, etc. The vinyl c.. |
|||
Tensile Strength, Ultimate | 17.6 MPa | 2550 psi | ASTM D638 |
Colorite Polymers 92-605 General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 17.6 MPa | 2550 psi | |
Colorite Polymers Self Frosting™ 8011SF Vinyl Compound Description: Colorite has developed a family of vinyl compounds to satisfy the needs of those who need a smooth, low gloss, low friction surface for the products that they produce. Historically, thi.. |