Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 16.5 MPa | 2390 psi | ASTM D638-95 |
Multibase Multi-Flex® TPO D 6713 Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 16.5 MPa | 2390 psi | ASTM D638-95 |
Multibase Multi-Pro® 4002 C BLK 40% Filler Content Polypropylene This product is a high impact PP copolymer developed for extrusion applications. The product lends itself well for automation of nail-gun operation, requiring good melt strength and impact resistan.. |
|||
Tensile Strength, Ultimate | 16.5 MPa | 2400 psi | TM R050-36 |
Resinlab® EP1294 Mineral Filled, Flame Retardant Epoxy Syntactic Foam Resinlab™ EP1294 is a two part mineral filled, flame retardant epoxy syntactic foam. It utilizes glass microspheres to reduce cured density and improve machinability. This product will be self-exti.. |
|||
Tensile Strength, Ultimate | 16.5 MPa | 2400 psi | ASTM D412 |
PB1100-60 Polyurethane-based Biomedical Elastomer |
|||
Tensile Strength, Ultimate | 16.5 MPa | 2390 psi | Machine direction |
Spartech Spectrum® S370 TPO Polyolefin Sheet
(discontinued **) Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 16.5 - 524 MPa | 2390 - 76000 psi | Average value: 126 MPa Grade Count:190 |
Overview of materials for Nylon 610 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 610". Each property range of values reported is minimum and maximum values of appropriate MatWeb e.. |
|||
Tensile Strength, Ultimate | 16.5 MPa | 2400 psi | |
Sylvin Technologies 6160-90 PVC Wire/Cable Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 16.5 MPa | 2400 psi | |
Sylvin Technologies 6161-82 PVC Wire/Cable Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 16.5 MPa | 2400 psi | |
Sylvin Technologies 8925-80 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 16.5 MPa | 2400 psi | |
Sylvin Technologies 8960-90 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 16.5 MPa | 2400 psi | |
Sylvin Technologies 916V0-95 Natural PVC for Injection Molding Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 16.5 MPa | 2400 psi | |
Sylvin Technologies 9925-80 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 16.5 MPa | 2400 psi | |
Sylvin Technologies 500 PVC Wire/Cable Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 16.5 MPa | 2400 psi | |
Sylvin Technologies 5132-75 PVC Wire/Cable Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 16.5 MPa | 2400 psi | |
Sylvin Technologies 578 PVC Wire/Cable Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 16.5 MPa | 2400 psi | |
Sylvin Technologies 6065 LT GL 85 PVC Wire/Cable Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 16.5 MPa | 2400 psi | |
Sylvin Technologies 6137-85 PVC Wire/Cable Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 16.5 MPa | 2400 psi | ASTM D638 |
Ecomass® 4703ZD90 Tungsten Filled Polyurethane Nontoxic alternative to Lead (Pb), weighting, balancing and radiation shielding applicationsModerate Specific GravityTungsten Filled Polyurethane (TPU)FlexibleInformation provided by Technical Polym.. |
|||
Tensile Strength, Ultimate | 16.5 MPa | 2400 psi | ASTM D638 |
Ecomass® 705ZG91 Stainless Steel/Tungsten Filled ABS High Specific GravityStainless Steel/Tungsten Powder Filled ABSInformation provided by Technical Polymers |
|||
Tensile Strength, Ultimate | 16.5 MPa | 2400 psi | ASTM D638 |
Ecomass® 720ZD91 Tungsten Filled ABS High Specific GravityTungsten Powder Filled ABSGood ToughnessPlateableInformation provided by Technical Polymers |
|||
Tensile Strength, Ultimate | 16.5 MPa | 2400 psi | ASTM D638 |
Colorite Polymers 7588 Non-Phthalate 88 Series Vinyl Compound Description: The Colorite 88 series is a family of vinyl non-toxic compounds formulated to provide excellent low temperature flexibility characteristics. These compounds are designed for outside doo.. |
|||
Tensile Strength, Ultimate | 16.5 MPa | 2390 psi | ASTM D638 |
Buckeye Polymers BP Flex D0853 TPO TPO's are a family of thermoplastic elastomers which exhibit rubber-like properties and are processable on conventional thermoplastic equipment. These resins have excellent UV resistance and have a.. |
|||
Tensile Strength, Ultimate | 16.5 MPa | 2390 psi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
DuPont Performance Polymers VTR 8525 (GBLT-S) GLT 505 Formulation
(discontinued **) FormulationViton® GLT 505 |
|||
Tensile Strength, Ultimate | 16.5 MPa | 2400 psi | |
Sylvin Technologies 5123 PVC Wire/Cable Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 16.5 - 32.0 MPa | 2390 - 4640 psi | Average value: 23.4 MPa Grade Count:11 |
Overview of materials for Polypropylene with Carbon Black Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with Carbon Black Filler". Each property range of values reported is minimum and maximum v.. |