Polymer Property : Tensile Strength, Ultimate = 15200 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 105 MPa
15200 psi
Same value from ASTM and ISO tests; 5 mm/min.
BASF Capron® HPN 9315G HS BK-102 Impact Modified, 15% Glass-Filled Nylon 6 (Dry)  (discontinued **)
Capron HPN 9315G HS BK-102 is a 15% glass reinforced impact modified, heat stabilized, pigmented black, nylon 6 injection molding grade resin. It is in the High Productivity Nylon Series developed ..
Tensile Strength, Ultimate 105 - 220 MPa
15200 - 31900 psi
Average value: 144 MPa Grade Count:29
Overview of materials for Polybutylene Terephthalate (PBT), 40% Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 40% Glass Fiber Filled". Specific grades with glass content between 35..
Tensile Strength, Ultimate 105 MPa
15200 psi
ASTM Data
Dow Questra® QA805 High Heat Syndiotactic Polystyrene, 30% Glass Filled  (discontinued **)
QUESTRA® Crystalline Polymers are semi-crystalline engineering thermoplastic resins produced from styrene monomer using a proprietary metallocene catalyst system. These syndiotactic polymers are ve..
Tensile Strength, Ultimate 105 MPa
15200 psi
ASTM Data
Dow Questra® WA552 High Heat Syndiotactic Polystyrene, 30% Glass Filled  (discontinued **)
QUESTRA® Crystalline Polymers are semi-crystalline engineering thermoplastic resins produced from styrene monomer using a proprietary metallocene catalyst system. These syndiotactic polymers are ve..
Tensile Strength, Ultimate 105 - 170 MPa

@Temperature 60.0 - 150 °C
15200 - 24700 psi

@Temperature 140 - 302 °F
Average value: 135 MPa Grade Count:1
Overview of materials for Nylon 66, Carbon Fiber/PTFE Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Carbon Fiber/PTFE Filled". Each property range of values reported is minimum and maximum value..
Tensile Strength, Ultimate 105 MPa
15200 psi
ASTM data at 5 mm/min.
BASF Capron® 8232G 25% Glass-Filled Nylon 6 (Conditioned)  (discontinued **)
Capron 8232G is a 25% glass fiber reinforced nylon 6 molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. Its resistance to creep under l..
Tensile Strength, Ultimate 105 MPa

@Temperature 980 °C
15200 psi

@Temperature 1800 °F
Haynes 214® alloy, cold rolled annealed sheet 2.0-3.2 mm thick
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Ultimate 105 MPa

@Temperature 1095 °C
15200 psi

@Temperature 2003 °F
Haynes HR-120® alloy, solution heat-treated plate
Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Tensile Strength, Ultimate 105 MPa
15200 psi
5mm/min; ISO 527
Styrolution Terblend® N NG-06 30% Glass Filled ABS/PA6 (Dry)
Terblend N NG-06 is a 30% glass fiber reinforced ABS/PA6 blend with extra high rigidity and dimensional stability.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS..
Tensile Strength, Ultimate 105 MPa
15200 psi
ISO 527-1, 2
Polyplastics Duranex® 3105 Polybutylene Terephthalate (PBT), Standard, 15% GF filled
DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Tensile Strength, Ultimate 105 MPa
15200 psi
ISO 527-1, 2
Polyplastics Duranex® 6300T Polybutylene Terephthalate (PBT), Low friction, Low wear, Mineral filled
DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Tensile Strength, Ultimate 105 MPa
15200 psi
ISO 527-1, 2
Polyplastics Duranex® 6302T Polybutylene Terephthalate (PBT), Low friction, Low wear, Mineral filled
DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Tensile Strength, Ultimate 105 MPa
15200 psi
ISO 527-1, 2
Polyplastics FR-PET® BN9015 Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Flame retardant, General purpose
Information provided by PolyPlastics.
Tensile Strength, Ultimate 105 MPa
15200 psi
ISO 527-1, 2
Polyplastics FR-PET® CN9015 Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Flame retardant, General purpose
Information provided by PolyPlastics.
Tensile Strength, Ultimate 105 MPa
15200 psi
ISO 527
Wellman Wellamid® GF13-66 22LH-N 13% Glass Fiber Reinforced Nylon 66, Lubricated & Heat Stabilized
Typical Applications: Radio and TV components, dishwasher roller carriages, chain saw oil reservoirs, gears, housings, door & window latches, power hand tool housings, high temperature devices.Data ..
Tensile Strength, Ultimate 105 MPa
15200 psi
ISO 527
Wellman Wellamid® MRGF30/10 42H-N 30% Mineral/10% Glass Fiber Reinforced Nylon 6, Heat Stabilized
Typical Applications: Lawn and garden equipment, automotive trim, bezels, wheel covers, window frames, gas tank filler housings, brackets, metalized lighting reflectors for automotive, automotive co..
Tensile Strength, Ultimate 105 MPa
15200 psi
ISO 527-1, 2
Polyplastics Duranex® 3105A Polybutylene Terephthalate (PBT), Epoxy adhesion improved, 15% GF filled
DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Tensile Strength, Ultimate 105 MPa

@Temperature 160 °C
15200 psi

@Temperature 320 °F
ISO 527-1/-2
DSM Stanyl® TW200B6 PA46-CF30
30% Carbon Reinforced, Heat Stabilized, Lubricated
Tensile Strength, Ultimate 105 MPa

@Temperature 180 °C
15200 psi

@Temperature 356 °F
ISO 527-1/-2
DSM Stanyl® TW271B6 (PA46+PTFE)-CF30
30% Carbon Reinforced, Heat Stabilized, Wear and Friction Modified
Tensile Strength, Ultimate 105 MPa
15200 psi
cond; ISO 527-1/-2
DSM Stanyl® TW271F6J10 (PA46+PTFE)-GF30
30% Glass Reinforced, Heat Stabilized, Wear and Friction Modified
Tensile Strength, Ultimate 105 MPa
15200 psi
ISO 527-1/-2
DSM Arnite® B434 SE PBT-GF20 FR(17)
20% Glass Reinforced, Flame Retardant
Tensile Strength, Ultimate 105 MPa
15200 psi
ISO 527-1/-2
DSM Arnite® B436 SE PBT-GF30 FR(17)
30% Glass Reinforced, Flame Retardant
Tensile Strength, Ultimate 105 MPa
15200 psi
5mm/min; ISO 527
BASF Petra® 110 BK-112 15% Glass Filled PET
Petra 110 is a 15% glass fiber reinforced, black pigmented, polyethylene terephthalate injection molding compound. It exhibits a good combination of performance properties including good strength a..
Tensile Strength, Ultimate 105 MPa
15200 psi
Diametral tensile strength
3M Z100™ Restorative Dental Composite
3M™ Z100™ restorative is an all purpose, esthetic, light cured dental composite. 3M Restorative Z100 features a translucency and opalescence similar to that of natural teeth and is used for porce..
Tensile Strength, Ultimate 105 MPa
15200 psi
ASTM D638
A. Schulman ComAlloy Hiloy® 515 Polycarbonate, Carbon Fiber Reinforced
Data provided by the manufacturer, ComAlloy International Company.10% Carbon Fiber Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate 105 MPa

@Temperature 538 °C
15200 psi

@Temperature 1000 °F
AK Steel Aluminized Carbon Steel, Commercial Steel (CS Type B), Standard Grade
Aluminized Type 1 coating contains approximately 91% aluminum and 9% silicon that is metallurgically bonded to the low-carbon steel substrate. May be moderately formed. A specimen cut in any direc..
Tensile Strength, Ultimate 105 MPa

@Temperature 300 °C
15200 psi

@Temperature 572 °F
Typical, after 10,000 hours
Aleris Weldural Aluminum Alloy, 100 mm Thickness
Sample treatment not specified for property data.Applications include precise mechanical parts with high dimensional stability, machine components, molds, and refrigeration engineering. Good weldab..
Tensile Strength, Ultimate 105 MPa
15200 psi
ISO 527
Sumitomo Bakelite North America RX® 790 Fiberglass Reinforced Phenolic Novolac
RX 790 is a fiberglass reinforced phenolic novolac compound, featuring a good balance of strength and toughness. Information supplied by Sumitomo Bak North America.
Tensile Strength, Ultimate 105 MPa
15200 psi
ASTM D638
Solvay Specialty Polymers Ixef® 2010/X914 Polyarylamide, 40% Filler, DAM  (discontinued **)
The IXEF compounds are a family of semi-crystalline polyarylamide thermoplastics reinforced with glass fibers and/or mineral fillers for injection molding.Data provided by the manufacturer, Solvay A..