Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | >= 1035 MPa | >= 150100 psi | |
Materion Nibryl Beryllium Nickel Alloy (Nibryl)-360 Rod and Bar; H925 (H925) Temper; All Sizes (UNS N03360) Tabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to Materion Corporation in March 2011. |
|||
Tensile Strength, Ultimate | >= 1035 MPa | >= 150100 psi | |
MetalTek MTEK M-152 Martensitic Stainless Steel "400" series, General corrosion resistant alloy, high strength.Applications: Chemical and food process equipment, jet engine compressor cases and rocket engine parts.Information provided by MetalTek.. |
|||
Tensile Strength, Ultimate | 1035 MPa | 150100 psi | |
Haynes 214® alloy, 20% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Tensile Strength, Ultimate | 1035 MPa | 150100 psi | Typical |
TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Sheet Medium To High Strength General-Purpose Alloy. Tensile property data below is typical of sheet; more specific form/thickness entries are also available in MatWeb.Industry Specifications: USA Aero.. |
|||
Tensile Strength, Ultimate | 1035 MPa | 150100 psi | |
Carpenter BioDur™ CCM® Medical Implant Alloy, Annealed Data provided by Carpenter Technology Corporation.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting high strength, corrosion resistance, and wear resistance. BioDur Carpenter CCM alloy.. |
|||
Tensile Strength, Ultimate | 1035 MPa @Temperature -196 °C |
150100 psi @Temperature -321 °F |
|
ATI Allegheny Ludlum Altemp® HX Nickel-Based superalloy Characteristics: outstanding resistance to oxidation at high temperatures, exceptional strength at elevated temperatures, good fabricability, good machinability in annealed condition, work hardening.. |
|||
Tensile Strength, Ultimate | 1035 MPa | 150100 psi | |
ATI Allvac® 6-2-4-2 Titanium Alloy, Heat Treatment: 982°C (1800°F) + Age Data provided by Allvac.Applications: High-temp jet engines. Blades, discs, spacers, seals. High performance automotive valves. Standard, rotor/premium grades. |
|||
Tensile Strength, Ultimate | 1035 MPa | 150100 psi | |
ATI Allvac® 6-2-4-2-Si UNS R54620 modified Titanium Alloy Uses: High performance valves for internal combustion engines. Aerospace and commercial grades.Property values are for samples in the metallurgical condition: 1800°F anneal.Information provided by .. |
|||
Tensile Strength, Ultimate | 1035 MPa | 150100 psi | |
ATI Allvac® 8-1-1 Titanium Alloy, Heat Treatment: 982°C (1800°F) + Age Data provided by Allvac.Applications: Fan & compressor blades, discs, spacers, seals, rings. Excellent creep resistance. Standard, rotor/premium grades. |
|||
Tensile Strength, Ultimate | 1035 MPa | 150100 psi | |
ATI Allvac® Nickelvac® A-286 Specialty Steel, Heat Treatment: 982°C (1800°F) + Age Data provided by Allvac.Applications: Jet engines, superchargers, missile components, fasteners, cryogenic equipment, nuclear, corrosive deep well hardware. |
|||
Tensile Strength, Ultimate | 1035 MPa | 150100 psi | |
ATI Allvac® Nickelvac® L-605 Cobalt-Nickel Superalloy, Heat Treatment: 1204°C (2200°F) Anneal Data provided by Allvac.Applications: High temperature applications, jet engine components, devices in high fatigue service. |
|||
Tensile Strength, Ultimate | 1035 MPa | 150100 psi | |
ATI Allvac® Vasco® 450 Specialty Steel, Heat Treatment: 1038°C (1900°F) + Age Data provided by Allvac.Applications: Land-based turbine blades and buckets. |
|||
Tensile Strength, Ultimate | 1035 MPa | 150100 psi | Longitudinal |
AK Steel 15-5 PH® Precipitation Hardening Stainless Steel, Condition H 1150 AK Steel 15-5 PH® provides high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), and good toughness in both base metal and welds. Short-time, .. |
|||
Tensile Strength, Ultimate | 1035 MPa | 150100 psi | |
ATI Allegheny Ludlum AL 15-5 High Strength Stainless Steel, UNS S15500 Property data below is typical of annealed samples. Available in plate. For use in fasteners, military equipment and air frame parts.Information provided by Allegheny Ludlum |
|||
Tensile Strength, Ultimate | <= 1035 MPa | <= 150100 psi | |
ATI Allegheny Ludlum Altemp® 718 Nickel-Base Superalloy, Solution Treated Plate, UNS N07718 Allegheny Ludlum Altemp 718 alloy is an austenitic nickel-base superalloy which is used in applications requiring high strength to approximately 760 degrees Celsius and oxidation resistance to appro.. |
|||
Tensile Strength, Ultimate | 1035 MPa | 150100 psi | |
Kennametal Stellite Stellite® 31 PM after P/M processing, aged 8 hours at 802°C air cooled Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous we.. |