Polymer Property : Tensile Strength, Ultimate = 15000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	103 - 124 MPa	15000 - 18000 psi	Average value: 115 MPa Grade Count:5
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 30% Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 30% Carbon Fiber Filled". Specific grades with carbon fiber conte..
Tensile Strength, Ultimate	103 MPa	15000 psi	Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Lubri-Tech™ PI-10CF/15T Polyetherimide (PEI), Carbon Fiber Reinforced, PTFE Lubricated (discontinued Description/Features:Carbon Fiber ReinforcedPTFE LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation.
Tensile Strength, Ultimate	103 - 221 MPa	15000 - 32100 psi	Average value: 155 MPa Grade Count:5
Overview of materials for Polyamide-Imide, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyamide-Imide, Glass Filled". Each property range of values reported is minimum and maximum values of ..
Tensile Strength, Ultimate	103 MPa	15000 psi
LE Phenolic Laminate Linen based phenolic provides more mechanical strength than paper grades and has a finer surface with better machinability. This material is used for gears, pinions, bearings, bushings, and many st..
Tensile Strength, Ultimate	103 MPa	15000 psi	Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Lubri-Tech™ SF-25GF/13T BLACK Polyphenylene Sulfide (PPS), Glass Filled, PTFE Lubricated (discontinue Description/Features:Glass Fiber ReinforcedPTFE LubricatedBlackPolyOne First ChoiceInformation provided by PolyOne Corporation.
Tensile Strength, Ultimate	103 MPa	15000 psi	ASTM D638
Techmer ES PlaslubeÂ® J-50/20/TF/10 Polycarbonate, 20% GFR, 10% PTFE
Tensile Strength, Ultimate	103 MPa	15000 psi
Williams Advanced Alloys WS217 Solder All Williams alloys are available in a variety of shapes and forms, including ribbon, preforms, rod, ring, wire, and custom shapes.Information provided by Williams Advanced Alloys
Tensile Strength, Ultimate	103 MPa @Temperature 927 °C	15000 psi @Temperature 1700 °F
Crucible Steel 321 Chromium-Nickel Steel Crucible 321 is a non-hardenable, low carbon austenitic chromium-nickel steel which is particularly adaptable for parts fabricated by welding without postweld annealing for use at temperatures betwe..
Tensile Strength, Ultimate	103 MPa	15000 psi	ASTM D638
Applied Composites 8049 Polyester SMC Industry Application: High StrengthProduct Application: MilitaryDistinct Features: High Impact Low Profile; Paintable/In Mold Coatable; Low Shrink; Low Moisture Absorption; Bondable; Formulated for ..
Tensile Strength, Ultimate	103.4 MPa @Temperature 982 °C	15000 psi @Temperature 1800 °F	1800°F
ATI Allegheny Ludlum Stainless Steel 334 (UNS S33400) Allegheny Ludlum Type 334 is a titanium- and aluminum-bearing austenitic stainless steel offering superior elevated temperature scaling resistance compared to the conventional chromium-nickel stainl..
Tensile Strength, Ultimate	103 - 166 MPa	15000 - 24000 psi	Average value: 143 MPa Grade Count:30
Overview of materials for Polycarbonate, 40% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 40% Glass Filled". Specific grades with glass content between 35% and 44% are included. E..
Tensile Strength, Ultimate	103 MPa	15000 psi	Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Edgetek® PS-20GF/000 FR Polybutylene Terephthalate (PBT), Glass Filled (discontinued **) Description/Features:Glass Fiber ReinforcedIgnition ResistantUL 94 V0PolyOne First ChoiceInformation provided by PolyOne Corporation.