Polymer Property : Tensile Strength, Ultimate = 1410 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	9.70 MPa	1410 psi	ASTM D638
Multibase Multi-Flex® TPE A 8502 P BLK , 37.5% Filler Content The following data represents the actual data obtained from Lot # 941101-5. The moisture content is 0.03%. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Tensile Strength, Ultimate	9.72 MPa	1410 psi	post cured- 4 hours at 204°C
Multibase SILASTIC® C7-4550 CADOX BSD Dow-Corning Biomedical Grade ETR Elastomer Information provided by Multibase
Tensile Strength, Ultimate	9.70 MPa	1410 psi	ASTM D638
Chevron Phillips 1006 LDPE Injection Molding Resin (discontinued **) Resin Type: homopolymerCharacteristics: excellent flexibility, excellent flow, good warping resistance, moderate mold release, moderate ESCRApplications: large housewares, tamper evident snap-on cap..
Tensile Strength, Ultimate	9.70 MPa	1410 psi	500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Eastman 1870A Polyethylene (discontinued **) Polyethylene 1870A is a low density formulation with excellent flow characteristics for injection molding. It is used for such applications as container closures that require stress-crack resistanc..
Tensile Strength, Ultimate	9.70 MPa	1410 psi	500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Eastman 808E Polyethylene (discontinued **) Low density polyethylene 808E is a general-purpose formulation used general-purpose extrusion. Under regulations administered by the US FDA, 808E may lawfully be used as articles or components of a..
Tensile Strength, Ultimate	9.70 MPa	1410 psi	500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Eastman E6838-850P Polyethylene (discontinued **) E6838-850P is a low density resin designed for applications where high coating speeds and good drawdown are required. The combination of high melt index and low density also provides good heat seal..
Tensile Strength, Ultimate	9.70 MPa	1410 psi	ASTM D638
NOVA Chemicals Novapol® LF-0222-A LDPE Wire and Cable Resin (discontinued **) NOVA Chemicals NOVAPOL® LF-0222-A is a medium molecular weight low density polyethylene. Resin consistency and purity are very high which make it suitable as a base resin in Wire and Cable applicat..
Tensile Strength, Ultimate	9.70 MPa	1410 psi	ISO 527-1/-2
DSM Arnitel® XG6029 TPC-ET Extrusion Grade
Tensile Strength, Ultimate	9.70 MPa	1410 psi
Dow Primacor® 5980I Ethylene Acrylic Acid (EAA) PRIMACOR® 5980I dispersible polymer is an ethylene acrylic acid copolymer (20 wt % comonomer) which is dispersible in aqueous alkali and amines. Excellent adhesion to metallic, cellulosic, glass an..
Tensile Strength, Ultimate	9.72 MPa	1410 psi	ASTM D412; ISO 37
Advanced Polymer Alloys Alcryn® 2265 UT Melt Processable Rubber Alcryn melt-processable rubber (MPR) is a true rubber, based on a partially cross-linked, chlorinated olefin interpolymer alloy. Alcryn is designed for the manufacture of rubber parts with high prod..
Tensile Strength, Ultimate	9.70 MPa	1410 psi	ASTM D638
Buckeye Polymers BP Flex D0840 TPO Replace Flex PVCTPO's are a family of thermoplastic elastomers which exhibit rubber-like properties and are processable on conventional thermoplastic equipment. These resins have excellent UV resis..