Polymer Property : Tensile Strength, Ultimate = 1360 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate >= 9.38 MPa
>= 1360 psi
ASTM D412
Multibase Multi-Flex® TPE A 7410 NAT
Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Tensile Strength, Ultimate 9.40 MPa
1360 psi
ASTM D412
Multibase Multi-Flex® TPE A 9402-SR BLK
Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Tensile Strength, Ultimate 9.40 MPa
1360 psi
ASTM D412-80
DuPont Performance Polymers Hypalon® 20 Chlorosulfonated Polyethylene Rubber, Mineral Filled Compound  (discon
Mineral filled compound with 100 parts Hypalon; 80 parts hard clay; 4 parts magnesia; 30 parts aromatic process oil; 3 parts pentaerythritol; and 2 parts Tetrone® A rubber accelerator (from DuPont ..
Tensile Strength, Ultimate 9.40 MPa
1360 psi
ISO 37
Green Dot Terratek® Flex GDH-B1 Compostable Bioplastic Elastomer
GDH-B1 is an elastomeric bioplastic with a diverse range of potential applications. It is a starch-based elastomer that is strong, durable and pliable with an exquisite soft touch. The bioplastic i..
Tensile Strength, Ultimate 9.38 MPa
1360 psi
Dow Corning S70 LIQUID SILICONE RUBBER KIT
A heat-cured elastomer for use by customers fabricating medical devices, including those intended for implantation in humans for less than 30 days and non-implant applications. Dow Corning® S70 Liq..
Tensile Strength, Ultimate 9.38 MPa
1360 psi
Dow Corning SILASTIC® LS 5-8725 FLUOROSILICONE RUBBER
25 Durometer, off-white, molding grade fluorosilicone base.Information provided by Dow Corning
Tensile Strength, Ultimate 9.38 MPa
1360 psi
Dow Corning SILASTIC® Q7-4550 BIOMEDICAL GRADE ETR ELASTOMER
One-part, enhanced tear-resistant silicone elastomers; uncatalyzed (customer selects peroxide catalyst) elastomer materials designed for compounding into elastomer for part fabrication and medical d..
Tensile Strength, Ultimate 9.40 MPa
1360 psi
ASTM D638-61T
Chevron Phillips 1018 Extrusion Coating Resin
Resin Type: High Speed ResinCharacteristics: Excellent Processability, High Temperature Stability, Good Draw Down ResinApplications:Food Packaging, Laminations, Sealant ResinData provided by Chevron..
Tensile Strength, Ultimate 9.40 MPa
1360 psi
Dow DOWLEX™ 2500 Linear Low Density Polyethylene, Narrow MW Distribution
DOWLEX® 2500 Polyethylene resin is a narrow molecular weight distribution copolymer designed to offer excellent environmental stress crack resistance and tear strength with high impact strength. It..