Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | Y direction; 0.1/min strain rate; ASTM D638 |
Rogers Corporation RT/duroid® 6010.2LM Ceramic-PTFE Composite Microwave Laminate Features:High dielectric constant for circuit size reductionLow loss - Ideal for operating at X-band or belowLow Z-axis expansion. Provides reliable plated through holes in multi-layer boardsTight .. |
|||
Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | |
3M Dyneon™ Fluorel™ FE-5610Q Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. The FE series O-ring grades are the c.. |
|||
Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | |
3M Dyneon™ Fluorel™ FC-2122 Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. Good flow, release and hot tear for c.. |
|||
Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | |
3M Dyneon™ Aflas® FA-150E PTFE Fluoroelastomer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Non-incorporated cure polymer, 57%F in polymer with 19% Medium Thermal Carbon Black (N990), 4% Triallyl Isocyanurate (TAIC), 1% Percadox™ 14, 1% Sodium.. |
|||
Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | |
3M Dyneon™ Fluorel™ FT-2430 Fluoroelastomer VF2 + HFP + TFE Terpolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Non-incorporated cure polymer, 69%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, 4% Ca(OH)2, 1.4% Dihydroxy Crosslinker, 0.4% Phospho.. |
|||
Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | ASTM Data |
Americas Styrenics Styron® 6187SF High Impact Polystyrene
(discontinued **) STYRON® 6187SF structural foam molding resin is a high impact polystyrene grade with proprietary ignition resistance additive package to achieve UL 94 V-0 rating. It offers excellent moldability an.. |
|||
Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | ASTM D638 |
Huntsman Rexell® H2109 Injection Molding LLDPE
(discontinued **) Linear-low high density injection molding.Features: High flow, good ESCR.Applications: General purpose molding, housewares.Information provided by Huntsman Corporation |
|||
Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | ASTM D638 |
Huntsman PE7076 Profile Extrusion Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Yields parts with high gloss and excellent stiffness.Applications: Extrusion: profile extrusion.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (c)2.2 u.. |
|||
Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | ASTM D638 |
ExxonMobil Escorene® LD-720 High EVA Film Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A high vinyl acetate copolymer specialty film resin designed for applications requiring outstanding heat sealability along with excellent strength p.. |
|||
Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | ASTM D638 |
Huntsman PE1407 EVA Film Extrusion
(discontinued **) 4% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: Fi.. |
|||
Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | ASTM D638 |
Global V-1160 High Density Polyethylene, Injection Molding Grade
(discontinued **) Description-opacity, medium high stiffness, good impact strength, good chemical resistanceApplications- auto parts, bottles, housewares, drums, containers, bottlesMeets FDA requirements as listed in.. |
|||
Tensile Strength, Ultimate | 13.0 - 36.0 MPa | 1890 - 5220 psi | Average value: 26.0 MPa Grade Count:91 |
Overview of materials for Polypropylene with 30% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Talc Filler". Specific grades with primary filler content between 25% and 34% are.. |
|||
Tensile Strength, Ultimate | 13.0 - 30.0 MPa | 1890 - 4350 psi | Average value: 20.4 MPa Grade Count:7 |
Overview of materials for Anhydride-Modified Polyethylene This property data is a summary of similar materials in the MatWeb database for the category "Anhydride-Modified Polyethylene". Each property range of values reported is minimum and maximum values o.. |
|||
Tensile Strength, Ultimate | 13.0 - 333 MPa | 1890 - 48300 psi | Average value: 34.2 MPa Grade Count:53 |
Overview of materials for Polytetrafluoroethylene (PTFE), Molded This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Molded". Each property range of values reported is minimum and maximum v.. |
|||
Tensile Strength, Ultimate | 13.0 - 35.0 MPa | 1890 - 5080 psi | Average value: 24.5 MPa Grade Count:32 |
Overview of materials for Polytetrafluoroethylene (PTFE), Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Extruded". Each property range of values reported is minimum and maximum.. |
|||
Tensile Strength, Ultimate | 13.0 - 16.0 MPa @Temperature 120 - 120 °C |
1890 - 2320 psi @Temperature 248 - 248 °F |
Average value: 14.5 MPa Grade Count:2 |
Overview of materials for Polychlorotrifluoroethylene; Molded This property data is a summary of similar materials in the MatWeb database for the category "Polychlorotrifluoroethylene; Molded". Each property range of values reported is minimum and maximum valu.. |
|||
Tensile Strength, Ultimate | 13.0 MPa @Thickness 2.00 mm |
1890 psi @Thickness 0.0787 in |
ASTM D4894 |
3M Dyneon™ TFM™ 4215 Modified PTFE, 25% Electrocarbon Filled
(discontinued **) Applications include bearings, seals/gaskets, packings, piston rings.Data provided by Dyneon. |
|||
Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | |
Freudenberg Simrit V174 Fluoroelastomer Self-Lube Additives to elastomer compounds can improve the lubricity or non-stick performance of a seal. Specific compound ingredients may include fluoropolymer (TEFLON) additives, silicone additives or molyb.. |
|||
Tensile Strength, Ultimate | 13.0 MPa @Temperature 22.0 °C |
1890 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® SMC 0520 Unsaturated Polyester UP SMC 0520 is a special SMC with significantly reduced density. The glass level has been selected to combine good moulding with sufficient strength and stiffness properties. Even without a specific fi.. |
|||
Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | |
Kuraray HYBRAR® HD1 Thermoplastic Rubber-HDPE Blend Description: HYBRAR® is another in the series of new high performance thermoplastic rubbers developed by KURARAY using their unique isoprene technology. HYBRAR® is a special thermoplastic rubb.. |
|||
Tensile Strength, Ultimate | 13.0 MPa @Temperature 49.0 °C |
1890 psi @Temperature 120 °F |
Type IV, crosshead speed 2 in/min; ASTM D638 |
DuPont Elvax® 670 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | Heat aged 2 weeks at 175°C |
DuPont Vamac® DP DIAK No. 7 Coagent Test Compound Vamac® DP is an ethylene acrylic dipolymer elastomer. Its general performance characteristics are similar to those of the Vamac® terpolymers, including:Good oil and chemical resistanceHigh temper.. |
|||
Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | Heat aged 2 weeks at 175°C |
DuPont Vamac® DP HVA-2 Coagent Test Compound Vamac® DP is an ethylene acrylic dipolymer elastomer. Its general performance characteristics are similar to those of the Vamac® terpolymers, including:Good oil and chemical resistanceHigh temper.. |
|||
Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | ASTM D638/D412 |
Covestro Baydur® 660 IBS Polyurethane Structural Foam RIM, Density 30 pcf, MDI-based 2-Component Liquid System 0.25 in. thickness. IBS = Interactive Blowing System RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience .. |
|||
Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | ISO 527-1 |
Dow BETAMATE™ XW 1185 Epoxy BETAMATE™ XW 1185 is a one component heat curing Epoxy paste adhesive. The material is readily pumped at ambient temperatures. It shows excellent adhesion to automotive steel and aluminum, is resi.. |
|||
Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | ASTM D638/D412 |
Covestro Bayflex® MP-5000 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System 0.118 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and of.. |
|||
Tensile Strength, Ultimate | 13.0 - 16.0 MPa @Temperature 120 °C |
1890 - 2320 psi @Temperature 248 °F |
ASTM D638 |
Arkema Group VOLTALEF® 302 PCTFE VOLTALEF® 302 is a chlorotrifluoroethylene dense powder. Used in particular for compression molding, non-flammable. Information provided by Arkema Group |
|||
Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | ASTM D638 |
Huntsman PE6076 Blow Molding Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Yields bottles with good clarity and excellent stiffness.Applications: Blow molding.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (c)2.2 under conditi.. |
|||
Tensile Strength, Ultimate | 13.0 - 105 MPa | 1890 - 15200 psi | Average value: 28.7 MPa Grade Count:73 |
Overview of materials for Polypropylene with 10% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 10% Talc Filler". Specific grades with primary filler content between 5% and 14% are .. |