Polymer Property : Tensile Strength, Ultimate = 128 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 128 MPa
18600 psi
ASTM D638
Owens Corning Glass Fiber Reinforced Acetal, 25 wt.% glass
Data provided by the manufacturer, Owens Corning.
Tensile Strength, Ultimate 128 MPa
18600 psi
ASTM D638
Solvay Specialty Polymers Amodel® A-1115 HS Polyphthalamide (PPA) Resin, 15% Glass Reinforced, Dry As Molded  
AMODEL A-1115 HS resin is a 15% glass reinforced, heat stabilized polyphthalamide (PPA) which exhibits a high deflection temperature, high flexural modulus, and high tensile strength. Excellent cre..
Tensile Strength, Ultimate 128 - 182 MPa
18500 - 26400 psi
Average value: 151 MPa Grade Count:5
Overview of materials for Liquid Crystal Polymer (LCP), Unfilled
This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), Unfilled". Each property range of values reported is minimum and maximum v..
Tensile Strength, Ultimate 128 MPa
18600 psi
Haysite 54500 Polyester SMC, 35% Glass Reinforced
A high strength fiberglass reinforced thermoset polyester compound formulated for injection, compression, or transfer molding. This material exhibits excellent electrical and mechanical properties, ..
Tensile Strength, Ultimate 128 MPa
18600 psi
ASMT D638
Toyobo TS101 PPS, Glass Fiber/Mineral Reinforced
Key Feature: High dimensional stabilityHigh performance injection-molding resin created from crystalline polyphenylene sulfide, using a special formulation technology developed by Toyobo. Excellent..
Tensile Strength, Ultimate 128 MPa
18600 psi
5 mm/min
Arkema Group Rilsan® ASR 20 Nylon 12, 20% Carbon Fiber Filled (Conditioned)
Designation ISO 1874-PA12,M,16-090,CF20Rigid grade with carbon fiber filler (20%) for injection molding. Available color: black. High strength-to-weight ratio. Very low shrinkage: include 0,5% on av..
Tensile Strength, Ultimate 128 MPa
18600 psi
ASTM D638
Chem Polymer Chemlon 225-15 MG Nylon 6, 25% Mineral/15% Glass Fiber Reinforced
A 25% mineral reinforced, 15% glass fiber reinforced nylon 6 offering excellent rigidity, dimensional stability and warpage control in large area parts.Data provided by the manufacturer, Chem Polyme..
Tensile Strength, Ultimate 128 MPa
18600 psi
ASTM D638
A. Schulman ComAlloy Hiloy® 612 Nylon 6, Glass Reinforced, UL
Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate 128 MPa
18600 psi
ASTM D638
A. Schulman ComAlloy Hiloy® 757 Carbon Fiber Reinforced, Flow Enhanced, PPS Alloy
Data provided by the manufacturer, ComAlloy International Company.30% Carbon Fiber Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate 128 MPa
18600 psi
ASTM D638
A. Schulman ComAlloy Lubrilon® 610 Nylon 6, Carbon Fiber/PTFE Reinforced
Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma..
Tensile Strength, Ultimate 128 MPa

@Temperature 60.0 °C
18600 psi

@Temperature 140 °F
ISO 527
LATI LARTON G/40 40% Glass Fiber Filled Polyphenylene sulfide (PPS)  (Unverified Data**)
Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex..