Polymer Property : Tensile Strength, Ultimate = 124000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	855 MPa @Temperature -80.0 °C	124000 psi @Temperature -112 °F	EN min; EN 10002-5
Outokumpu 4541 Cr-Ni Austenitic Stainless Steel Good corrosion resistance and weldable. Resistant to sensitization.Applications: Welded screensFurnace beltsCatalytic converter meshAvailable in hot rolled plate (Quarto), hot rolled strip/sheet (C..
Tensile Strength, Ultimate	855 MPa	124000 psi	Typical
Kinetics MIM K3 Heat Treat as Sintered K3 is a custom Mo-Fe alloy that provides improved fatigue properties over many other steel alloys while still maintaining good strength components, industrial or structural components and other appl..
Tensile Strength, Ultimate	855 MPa	124000 psi	4 in. Test Specimen
Latrobe LescalloyÂ® 410Cb High Strength Stainless Steel LESCALLOY 17-4 VAC-ARC steel is a precipitation hardening martensitic stainless steel. A wide range of mechanical properties is available via simple aging within a 900-1150Â°F (482-621Â°C) tempe..
Tensile Strength, Ultimate	852 MPa	124000 psi
Haynes HastelloyÂ® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871Â°C (1600Â°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Tensile Strength, Ultimate	858 MPa @Temperature 760 Â°C	124000 psi @Temperature 1400 Â°F
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, air cooled, aged 16 hours at 760Â°C (1400Â°F) Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Tensile Strength, Ultimate	855 MPa @Temperature 540 Â°C	124000 psi @Temperature 1000 Â°F
Haynes 263Â® alloy, cold rolled sheet, solution treated and aged Very good aged strength properties, excellent fabrication characteristics when annealed, excellent intermediate temperature tensile ductility, is not normally subject to strain age cracking, excelle..
Tensile Strength, Ultimate	855 MPa @Temperature 760 Â°C	124000 psi @Temperature 1400 Â°F
Haynes 718 alloy, cold rolled, solution-treated and aged sheet Cb and Ta content combined weight percentage of 5. Excellent high-temperature strength up to 650Â°C, good ductility, formability, and weldability. Very good welding characteristics. Applications i..
Tensile Strength, Ultimate	855 MPa	124000 psi
Special Metals INCONELÂ® 725 Nickel Superalloy (UNS N07725), Annealed Round Tensile strength (ultimate and yield), hardness, and elongation values reported here are typical for Annealed Round samples. Other property values are typical of INCONELÂ® alloy 725.Data provided..
Tensile Strength, Ultimate	855 MPa @Temperature 316 °C	124000 psi @Temperature 600 °F	H1150
Crucible Steel 15-5 Precipitation Hardening Stainless Steel Crucible 15-5 is a Premium Quality precipitation-hardening stainless steel which is capable of high strength and hardness levels after a relatively simple heat-treatment procedure. This grade is a V..
Tensile Strength, Ultimate	855 MPa @Temperature 316 °C	124000 psi @Temperature 600 °F	H1150
Crucible Steel 17Cr-4Ni Precipitation Hardening Stainless Steel Crucible 17Cr-4Ni is a precipitation-hardening stainless steel which is capable of a high strength and hardness levels after a relatively simple heat-treatment procedure. This grade is martensitic a..
Tensile Strength, Ultimate	855 MPa @Temperature 316 °C	124000 psi @Temperature 600 °F	H1150
Crucible Steel 17Cr-4Ni Super-X® Precipitation Hardening Stainless Steel Crucible 17Cr-4Ni is a version of 17CR-4Ni which has been modified to substantially improve machinability and other properties. Patented 17Cr-4Ni Super-X meets industry specifications for 17Cr-4Ni. ..
Tensile Strength, Ultimate	855 MPa @Thickness 22.2 mm	124000 psi @Thickness 0.875 in	Typical for Plate, Annealed
AK Steel NITRONIC® 30 Austenitic Stainless Steel AK Steel NITRONIC 30 Stainless Steel offers significantly higher strength than Type 304 and potential for applications requiring good resistance to aqueous and atmospheric corrosion resistance combi..
Tensile Strength, Ultimate	855 MPa	124000 psi
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 10% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i..