Polymer Property : Tensile Strength, Ultimate = 1190 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 8.20 MPa
1190 psi
post cured- 2 hours at 177°C
Multibase SILASTIC® C7-4535 CADOX TS-50S Dow-Corning Biomedical Grade ETR Elastomer
Information provided by Multibase
Tensile Strength, Ultimate 8.20 MPa
1190 psi
as molded
Multibase SILASTIC® C7-4565 DICUP R Dow-Corning Biomedical Grade ETR Elastomer
Information provided by Multibase
Tensile Strength, Ultimate 8.20 MPa
1190 psi
no post cure; ASTM D412
Multibase C6-530 Dow-Corning Class VI Elastomer
Information provided by Multibase
Tensile Strength, Ultimate 8.24 MPa
1190 psi
500 mm/min; ASTM D 412
Zylog Neoplast® 173 FT EB Thermoplastic Vulcanizate
Neoplast 173 FT EB is a soft, dynamically vulcanized thermoplastic vulcanizate (TPV), based on polyolefin chemistry, and is intended for Injection Molding, Blow Molding and Extrusion applications.Ro..
Tensile Strength, Ultimate 8.20 MPa
1190 psi
Dow Corning C6-530 LIQUID SILICONE RUBBER KIT
Dow Corning® Class VI Elastomers are heat cured elastomer raw materials for use by customers fabricating medical devices and partsInformation provided by Dow Corning
Tensile Strength, Ultimate 8.20 MPa
1190 psi
Dow Corning SILASTIC® LS 4-9040 FLUOROSILICONE RUBBER
40 Durometer, off-white, uncatalysed Fluorosilicone Base.Information provided by Dow Corning
Tensile Strength, Ultimate 8.20 MPa
1190 psi
Dow DOWLEX™ 2503 Linear Low Density Polyethylene, Narrow MW Distribution
DOWLEX® 2503 Polyethylene resin is a narrow molecular weight distribution copolymer designed to offer excellent environmental stress crack resistance and tear strength with excellent rigidity. It h..
Tensile Strength, Ultimate 8.20 MPa
1190 psi
ASTM D412-80
DuPont Performance Polymers Hypalon® 20 Chlorosulfonated Polyethylene Rubber, Gum Compound  (discontinued **)&
Gum compound with 100 parts Hypalon; 4 parts high activity magnesia; 3 parts pentaerythritol; and 2 parts Tetrone® A rubber accelerator (from DuPont Dow Elastomers). Reinforcing fillers recommende..