Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 7.79 MPa | 1130 psi | post cured- 2 hours at 177°C |
Multibase SILASTIC® C7-4565 VAROX Dow-Corning Biomedical Grade ETR Elastomer Information provided by Multibase |
|||
Tensile Strength, Ultimate | 7.80 MPa | 1130 psi | ISO 37 |
Multibase TPSiV® 4200-80A Thermoplastic Elastomer FEATURES & BENEFITS: Soft silky feel; Excellent abrasion and scratch resistance; Excellent bonding to PC, ABS; Good chemical resistanceAPPLICATIONS: Solution for soft touch overmolding on consumer e.. |
|||
Tensile Strength, Ultimate | 7.79 MPa | 1130 psi | post cured- 8 hours at 177°C; ASTM D412 |
Multibase C6-350 LH Parts A and B Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
Tensile Strength, Ultimate | 7.80 MPa | 1130 psi | GB/T 528 |
Chengdu Polyster FR2085 Flame Retardant Grade TPV Good heat stability and light stability. Meets the requirements of European Dioxine Principle and the environmental protection criteria. Can be used for wires, cables, buncles, carcass of train.Inf.. |
|||
Tensile Strength, Ultimate | 7.79 MPa | 1130 psi | |
Dow Corning HV 1540/20P BASE AND CLEAR CURING AGENT 32 Shore, very low viscosity, castable hydrophobic silicone rubber with high tear strength and low temperature cure.Information provided by Dow Corning |
|||
Tensile Strength, Ultimate | 7.79 MPa | 1130 psi | |
Dow Corning SILASTIC® Q7-4780 BIOMEDICAL GRADE ETR ELASTOMER, KIT Two-part, platinum-catalyzed (1:1 by weight), enhanced tear-resistant silicone elastomers are heat cured high consistency silicone rubbers designed for use by customers fabricating medical devices.I.. |