Polymer Property : Tensile Strength, Ultimate = 11200 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 77.2 - 234 MPa
11200 - 34000 psi
Average value: 175 MPa Grade Count:12
Overview of materials for Polyphenylene Sulfide (PPS) with 40% Carbon Fiber Filler
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 40% Carbon Fiber Filler". Specific grades with carbon fiber content bet..
Tensile Strength, Ultimate 77.0 - 281.306 MPa

@Temperature -40.0 - 150 °C
11200 - 40800.1 psi

@Temperature -40.0 - 302 °F
Average value: 104 MPa Grade Count:4
Overview of materials for Nylon 6, 40% Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. E..
Tensile Strength, Ultimate 76.9 MPa
11200 psi
MMCC Aluminum/Graphite Fiber GA 7-230 Metal Matrix Composite
Discontinuous graphite fiber aluminum product primarily used for electronic thermal management applications. Lightweight, high damping, stiffer than aluminum, matched cte, easily machined and plate..
Tensile Strength, Ultimate 77.0 MPa

@Temperature 1095 °C
11200 psi

@Temperature 2003 °F
Haynes 718 alloy, cold rolled, solution-treated and aged sheet
Cb and Ta content combined weight percentage of 5. Excellent high-temperature strength up to 650°C, good ductility, formability, and weldability. Very good welding characteristics. Applications i..
Tensile Strength, Ultimate 77.0 MPa
11200 psi
ISO 527-1, 2
Polyplastics Duranex® CTN7133 Polybutylene Terephthalate (PBT), Higher comparative tracking index, FR, GF filled
DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Tensile Strength, Ultimate 77.0 MPa
11200 psi
ISO 527-2/1A/5
Lubrizol ESTALOC® T5160 Ether-Type, Reinforced Engineering Thermoplastic (European Grade)
Description: Estaloc® RETP (Reinforced Engineering Thermoplastic) is a tough, dimensionally stable, abrasion-resistant thermoplastic that withstands demanding environments. Developed as an extensio..
Tensile Strength, Ultimate 77.0 MPa
11200 psi
dry; ISO 527-1/-2
DSM Novamid® 1010GN7-20 BK37 PA6-GF20 FR(30) 0
20% Glass Reinforced, Flame Retardant, Halogen free
Tensile Strength, Ultimate 77.2 MPa
11200 psi
BCC Products BC 5003 Epoxy Laminating System
BC 5003 is a medium viscosity, unfilled laminating system. It is a room temperature curing resin with a relatively short pot life. BC 5003 is also considered an excellent general purpose adhesive fo..
Tensile Strength, Ultimate 77.0 MPa
11200 psi
ASTM D638
A. Schulman ComAlloy Hiloy® 113 Polypropylene, Glass Reinforced, Chemically Coupled
Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate 77.0 MPa
11200 psi
ASTM D638
A. Schulman ComAlloy Hiloy® 249 SAN, Glass Reinforced
Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate 77.0 MPa
11200 psi
ASTM D638
A. Schulman ComAlloy Hiloy® 262 Glass Reinforced, Modified SMA
Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate 77.0 MPa
11200 psi
ASTM D638
Aardvark Polymers Aarlon® 2000 Rotational Molding Resin, 50% RH
Aarlon® 2000 PA 6/6 is a high performance nylon for rotational molding applications. Aarlon® 2000 offers high heat capabilities with exceptional mechanical properties.Information provided by Gehri..
Tensile Strength, Ultimate 77.0 MPa
11200 psi
ASTM D638
Plenco 1510 Polyester, Granular, Transfer Molded
PLENCO 01510 is a mineral filled, pelletized polyester molding compound, which offers an excellent combination of electrical properties and dimensional stability. UL recognized under component file ..
Tensile Strength, Ultimate 77.0 MPa
11200 psi
ASTM D638
Plenco 1581 Polyester, Briquette, Transfer Molded
PLENCO 01581 is a glass and mineral reinforced pelletized polyester molding compound, exhibiting excellent dimensional stability, mechanical strength and also arc resistance, track resistance, and f..
Tensile Strength, Ultimate 77.22 MPa
11200 psi
Phenolic 30%, Graphite fabric 70%
Phenyl silane - C.T.L "37-9X". Graphite fabric - "WCB"