Polymer Property : Tensile Strength, Ultimate = 112 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 112 MPa
16200 psi
ASTM D638
Solvay Specialty Polymers Amodel® A-1115 HS Polyphthalamide (PPA) Resin, 15% Glass Reinforced, at 50% RH  (dis
AMODEL A-1115 HS resin is a 15% glass reinforced, heat stabilized polyphthalamide (PPA) which exhibits a high deflection temperature, high flexural modulus, and high tensile strength. Excellent cre..
Tensile Strength, Ultimate 112 - 195 MPa
16200 - 28300 psi
Average value: 150 MPa Grade Count:11
Overview of materials for Polyphenylene Sulfide (PPS) Alloy, Glass Reinforced, Flow Enhanced
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) Alloy, Glass Reinforced, Flow Enhanced". Each property range of values repor..
Tensile Strength, Ultimate 112 MPa
16200 psi
ASTM D882
Honeywell Capran® 512 LL Heat Stabilized Nylon Film  (discontinued **)
Description: Capran® 512 LL is a heat-stabilized blown film produced from low lactam nylon-6 resin. It is recommended as bagging film for advanced composite fabrication and other high temperature ..
Tensile Strength, Ultimate 112 MPa
16200 psi
ASTM D882
Honeywell Capran® 518 LL Heat Stabilized Nylon Film  (discontinued **)
Description: Capran® 518 LL is a green tinted, heat-stabilized blown film produced from low lactam nylon-6 resin. It is recommended as bagging film for advanced composite fabrication and other hig..
Tensile Strength, Ultimate >= 112 MPa
>= 16200 psi
re-crystallized
H.C. Starck Pure Niobium (Columbium)
Applications: NRC® niobium metal is produced from electron beam melted ingots. Grain Stabilized Niobium (GSNb) is made by EB and VAR melting. Both materials are malleable, weldable, machineabl..
Tensile Strength, Ultimate 112 MPa
16200 psi
ISO 527-1/-2
DSM Arnite® TV4 441 (PBT+PET)-GF20
20% Glass Reinforced
Tensile Strength, Ultimate 112 MPa
16200 psi
ASTM D638
A. Schulman ComAlloy Comtuf® 633 Nylon 6/6, Glass Reinforced, Impact Modified, Flow Enhanced
Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int..
Tensile Strength, Ultimate 112 MPa
16200 psi
5 mm/min
Arkema Group Rilsan® AZM 30 NOIR T6LD Nylon 12, 30% Glass Fiber Filled (Dry)
Designation ISO 1874-PA12,MHLR,16-060,GF30Rigid grade with glass fiber (30%) for injection molding. Available color: black. Reinforced light and heat stabilizing agent. Mold-release agent.High rigid..
Tensile Strength, Ultimate 112 MPa
16200 psi
5 mm/min
Arkema Group Rilsan® BZM 30 TL Nylon 11, 30% Glass Fiber Filled (Conditioned)
Designation ISO 1874-PA11,MHL,18-050,GF30Rigid grade with glass fiber (30%) filler for injection molding. Available colors: black and natural. Light and heat stabilized.Rigidity. High compressive st..
Tensile Strength, Ultimate 112 MPa
16200 psi
ATSM D638
Ashley Polymers Ashlene® P266 PPO, 30% Glass Reinforced
A general purpose, 30% glass reinforced PPO resin for injection molding applications.Data provided by the manufacturer
Tensile Strength, Ultimate 112 MPa

@Temperature 60.0 °C
16200 psi

@Temperature 140 °F
ISO 527
LATI LARIL 13 G/30 30% Glass Fiber Reinforced Polyphenylene Oxide (PPOm)  (Unverified Data**)
Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most ..
Tensile Strength, Ultimate 112 MPa
16200 psi
ASTM D638
A. Schulman ComAlloy Hiloy® 756 Carbon Fiber Reinforced, Flow Enhanced, PPS Alloy
Data provided by the manufacturer, ComAlloy International Company.20% Carbon Fiber Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate 112 MPa
16200 psi
Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Edgetek® PI-10GF/000 Polyetherimide (PEI), Glass Filled  (discontinued **)
Description/Features:Glass Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.