Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 10.1 MPa | 1460 psi | ASTM D412 |
Multibase Multi-Flex® TPE D 4308 BLK The moisture content is 0.04%. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 10.1 MPa | 1460 psi | as molded |
Multibase SILASTIC® C7-4550 CADOX TS-50S Dow-Corning Biomedical Grade ETR Elastomer Information provided by Multibase |
|||
Tensile Strength, Ultimate | 10.1 MPa | 1470 psi | no post cure, press cured for 5 minutes; ASTM D412 |
Multibase SILASTIC® Q7-4850 Dow-Corning Biomedical Grade Liquid Silicone Rubber Information provided by Multibase |
|||
Tensile Strength, Ultimate | 10.1 MPa | 1460 psi | |
Dow Corning SILASTIC® 94-595-HC SILICONE RUBBER PART A&B 30 Durometer, 2-part, 1 to 1 mix, translucent, Injection Moulding grade, Liquid Silicone Rubber.Information provided by Dow Corning |
|||
Tensile Strength, Ultimate | 10.1 MPa | 1460 psi | |
Dow Corning SILASTIC® LS 5-8740 FLUOROSILICONE RUBBER BASE 40 Durometer off-white, molding grade fluorosilicone base.Information provided by Dow Corning |
|||
Tensile Strength, Ultimate | 10.1 MPa | 1470 psi | |
Dow Corning SILASTIC® LS-2840 FLUOROSILICONE RUBBER 40 Durometer, off-white, uncatalysed, moulding grade fluorosilicone baseInformation provided by Dow Corning |
|||
Tensile Strength, Ultimate | 10.1 MPa | 1470 psi | |
Dow Corning SILASTIC® Q7-4850 BIOMEDICAL GRADE ETR ELASTOMER, KIT Silastic® BioMedical Grade Liquid Silicone Rubbers are heat cured elastomer raw materials for use by customers fabricating medical devices.Information provided by Dow Corning |
|||
Tensile Strength, Ultimate | 10.1 MPa | 1460 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
Dow Nordel® IP 4640 General Purpose Compound FormulationNordel® IP 4640 |
|||
Tensile Strength, Ultimate | 10.1 MPa | 1460 psi | |
Dow Corning SILASTIC® LS-2860 FLUOROSILICONE RUBBER 60 Durometer, off-white, uncatalysed, moulding grade fluorosilicone baseInformation provided by Dow Corning |