Polymer Property : Peel Strength = 26.0 pli Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Peel Strength 4.56 kN/m

@Temperature 121 °C
26.0 pli

@Temperature 250 °F
T-Peel, 90 min @ 350°F, Spring Clamp Pressure, FPL Acid Etched 6061-T6; ASTM D1876
Zyvex Performance Materials Aroply™ 350 Nano-Engineered Composite Film Adhesive
Aroply™ 350 Film Adhesive is a versatile, heat curing carbon-nanotube modified epoxy structural film adhesive available in a variety of film weights on a supported carrier. Cured adhesive character..
Peel Strength 4.56 kN/m

@Temperature 82.2 °C
26.0 pli

@Temperature 180 °F
Bell Peel
Hexcel® Redux® 609 (0.06 psf) Adhesive film for bonding metallic and composite components
Redux 609 is a 250°F curing modified epoxy film adhesive containing a cottom scrim for easy handling and glue-line thickness control. It is available at standard areal weights of 0.06 psf and 0.04 ..
Peel Strength 4.56 kN/m

@Temperature 60.0 °C,
Time 605000 sec
26.0 pli

@Temperature 140 °F,
Time 168 hour
JRF/SW, Stainless Steel; AMS-S83318
3M AC-250 A-1/6 Aerospace Sealant
3M Aerospace Sealant AC-250 A-1/6 is a two-part, low temperature curing polysulfide, quick repair sealant for integral fuel tank and fuselage sealing applications. The mixed compound is a pourable l..
Peel Strength 4.56 kN/m

@Temperature 60.0 °C,
Time 605000 sec
26.0 pli

@Temperature 140 °F,
Time 168 hour
JRF, Alodine; AMS-S83318
3M AC-250 A-1/6 Aerospace Sealant
3M Aerospace Sealant AC-250 A-1/6 is a two-part, low temperature curing polysulfide, quick repair sealant for integral fuel tank and fuselage sealing applications. The mixed compound is a pourable l..
Peel Strength 4.56 kN/m

@Temperature 24.0 °C,
Time 259000 sec
26.0 pli

@Temperature 75.2 °F,
Time 72.0 hour
180°, Canvas/Steel
3M Scotch-Weld™ 1099-L Nitrile High Performance Plastic Adhesives
Features: It is a low viscosity grade for spray application.Fast dryingProvides strong, flexible bonds.Resists weathering, water, fuels, oil and plasticizers.Bonds vinyl extrusions and sheeting. (Ma..
Peel Strength 4.56 kN/m

@Temperature 82.0 °C,
Time 1.81e+6 sec
26.0 pli

@Temperature 180 °F,
Time 504 hour
180°, Canvas/Steel
3M Scotch-Weld™ 1300 Neoprene High Performance Rubber Gasket Adhesives
3M™ Scotch-Weld™ Neoprene High Performance Rubber ^& Gasket Adhesives 1300 is the most versatile of our rubber and gasket adhesives. They may be used to bond metal, wood, most plastics, and neopre..
Peel Strength 4.56 kN/m

@Temperature 24.0 °C,
Time 605000 sec
26.0 pli

@Temperature 75.2 °F,
Time 168 hour
180°, Canvas/Steel
3M Scotch-Weld™ 1357 Neoprene High Performance Contact Adhesive
3M™ Scotch-Weld™ Neoprene High Performance Contact Adhesive can be used to bond most rubber, cloth, metal, wood, foamed glass, paper honeycomb, decorative plastic laminates and many other substrat..
Peel Strength 4.56 kN/m

@Temperature 24.0 °C,
Time 605000 sec
26.0 pli

@Temperature 75.2 °F,
Time 168 hour
180°, Canvas/Steel
3M Scotch-Weld™ 1357-L Neoprene High Performance Contact Adhesive
3M™ Scotch-Weld™ Neoprene High Performance Contact Adhesive can be used to bond most rubber, cloth, metal, wood, foamed glass, paper honeycomb, decorative plastic laminates and many other substrat..
Peel Strength 4.56 kN/m

@Temperature 24.0 °C,
Time 259000 sec
26.0 pli

@Temperature 75.2 °F,
Time 72.0 hour
180°, Canvas/Steel
3M Scotch-Weld™ 4491 Nitrile Industrial Adhesive
Features: Low viscosity grade for spray applicationFast dryingProvides strong, flexible bondsResists weathering, water, fuels, oil and plasticizersBonds vinyl extrusions and sheeting (May stain ligh..
Peel Strength 4.56 kN/m

@Temperature 24.0 °C,
Time 259000 sec
26.0 pli

@Temperature 75.2 °F,
Time 72.0 hour
180°, Canvas/Steel
3M Scotch-Weld™ 1099 Nitrile High Performance Plastic Adhesives
Features: It is a medium viscosity grade for most brush or flow applicationsFast dryingProvides strong, flexible bonds.Resists weathering, water, fuels, oil and plasticizers.Bonds vinyl extrusions a..
Peel Strength 4.56 kN/m

@Temperature 82.0 °C,
Time 1.81e+6 sec
26.0 pli

@Temperature 180 °F,
Time 504 hour
180°, Canvas/Steel
3M Scotch-Weld™ 1300L Neoprene High Performance Rubber Gasket Adhesives
3M™ Scotch-Weld™ Neoprene High Performance Rubber ^& Gasket Adhesives 1300 is the most versatile of our rubber and gasket adhesives. They may be used to bond metal, wood, most plastics, and neopre..