Polymer Property : Peel Strength = 2.45 kN/m Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Peel Strength	2.45 kN/m @Temperature -34.0 °C, Time 1.81e+6 sec	14.0 pli @Temperature -29.2 °F, Time 504 hour	180°, Canvas/Steel
3M Scotch-Weld™ 2141 Neoprene Rubber & Gasket Adhesive Features: Alight colored, high strength adhesive with a long tack rangeExcellent water, oil and grease resistanceBonds neoprene, natural, reclaim SB-R and butyl rubber to most substrates.Information..
Peel Strength	2.45 kN/m @Temperature 24.0 °C, Time 432000 sec	14.0 pli @Temperature 75.2 °F, Time 120 hour	180°, Canvas/Steel
3M Scotch-Weld™ 5 Neoprene Contact Adhesive 3M™ Scotch-Weld™ Neoprene Contact Adhesive 5 is a sprayable contact adhesive which may be used to bond many high-pressure plastic laminates to wood, particle-board, metal and other surfacesInforma..
Peel Strength	2.45 kN/m @Time 259000 sec	14.0 pli @Time 72.0 hour	Adhesion to Truck Paint; ASTM D3330
3M 4411N Extreme Sealing Tape 3M™ Extreme Sealing Tape is a family of single coated, pressure sensitive adhesive tapes designed for difficult sealing applications. The backing on this tape is an ionomer film that is very tough ..
Peel Strength	2.45 kN/m @Temperature 82.0 °C, Time 1.81e+6 sec	14.0 pli @Temperature 180 °F, Time 504 hour	180°, Canvas/Steel
3M Fastbond™ 4213-NF Industrial Adhesive 3M™ Fastbond™ Industrial Adhesive 4213-NF is a white, water dispersed adhesive for bonding many fabrics, supported vinyl, wood, leather and most porous materials. Exhibits outstanding clarity when..
Peel Strength	2.45 kN/m @Temperature -34.0 °C, Time 1.81e+6 sec	14.0 pli @Temperature -29.2 °F, Time 504 hour	180°, Canvas/Steel
3M Scotch-Weld™ 4799 Industrial Adhesive 3M™ Scotch-Weld™ Industrial Adhesive 4799 can be used to bond most EPDM rubber, sponge rubber, rubber sheeting, felt, canvas, linoleum and other lightweight materials to many metals, woods, concre..