Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 50.0 MPa @Temperature 100 °C |
7250 psi @Temperature 212 °F |
ISO 527 |
BASF Ultradur B 4300 G2 10% Glass Filled PBT Ultradur B4300 G2 is an easy flowing injection molding PBT with 10% glass fiber reinforcement for rigid, tough, and dimensionally stable parts.Applications: Program switches, thermostat parts, small.. |
|||
Tensile Strength | 50.0 MPa @Time 1.81e+7 sec |
7250 psi @Time 5040 hour |
Storage in fuel CM15<sub>A</sub>P at +60°C |
BASF Ultraform S 2320 003 UNC Q600 POM Ultraform S2320 003 UNC Q600 is an easy flowing and rapidly freezing injection molding POM grade. Contains a mold release agent. |
|||
Tensile Strength | 50.0 MPa @Strain 5.00 %, Temperature 80.0 °C |
7250 psi @Strain 5.00 %, Temperature 176 °F |
50mm/min |
BASF Ultramid® KR 4350 PA6/6T (Dry) Description: For injection-molding and extrusion, exhibiting high toughness, strength and stiffness, low water absorption, high melting point (295 °C [563°F]). The mechanical properties remain con.. |
|||
Tensile Strength | 50.0 MPa @Strain 8.00 %, Temperature 80.0 °C |
7250 psi @Strain 8.00 %, Temperature 176 °F |
50mm/min |
BASF Ultramid® KR 4350 PA6/6T (Dry) Description: For injection-molding and extrusion, exhibiting high toughness, strength and stiffness, low water absorption, high melting point (295 °C [563°F]). The mechanical properties remain con.. |
|||
Tensile Strength | 50.0 MPa @Strain 2.00 %, Temperature 100 °C |
7250 psi @Strain 2.00 %, Temperature 212 °F |
5mm/min |
BASF Ultramid® KR 4355 G7 35% Glass Filled PA6/6T (Dry) Description: 35% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties r.. |