Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 40.0 MPa @Strain 2.00 %, Temperature 80.0 °C |
5800 psi @Strain 2.00 %, Temperature 176 °F |
50mm/min |
BASF Ultramid® KR 4350 PA6/6T (Dry) Description: For injection-molding and extrusion, exhibiting high toughness, strength and stiffness, low water absorption, high melting point (295 °C [563°F]). The mechanical properties remain con.. |
|||
Tensile Strength | 40.0 MPa @Strain 2.00 %, Temperature 150 °C |
5800 psi @Strain 2.00 %, Temperature 302 °F |
5mm/min |
BASF Ultramid® KR 4355 G7 35% Glass Filled PA6/6T (Dry) Description: 35% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties r.. |
|||
Tensile Strength | 40.0 MPa @Temperature 70.0 °C |
5800 psi @Temperature 158 °F |
5mm/min (0.2in/min); ASTM D638 |
DuPont Performance Polymers Delrin® 577 BK000 Acetal Homopolymer
(Unverified Data**) Delrin® 577 BK000 is a medium viscosity acetal homopolymer containing 20% glass fiber filler, with high stiffness, low warpage and low creep for superior performance at elevated temperature. It con.. |
|||
Tensile Strength | 40.0 MPa @Strain 3.00 %, Temperature 60.0 °C |
5800 psi @Strain 3.00 %, Temperature 140 °F |
ISO 527 |
BASF Ultramid® B3S HP PA6 (Dry) Ultramid B3S HP is a easy flowing, finely crystalline, injection molding PA6 for fast processing |
|||
Tensile Strength | 40.0 MPa @Strain 1.00 %, Temperature -20.0 °C |
5800 psi @Strain 1.00 %, Temperature -4.00 °F |
ISO 527 |
BASF Ultramid® B3S HP PA6 (Dry) Ultramid B3S HP is a easy flowing, finely crystalline, injection molding PA6 for fast processing |