Polymer Property : Tensile Strength = 16000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength 110 MPa

@Temperature -40.0 °C
16000 psi

@Temperature -40.0 °F
50%RH; ASTM D638
DuPont Performance Polymers Zytel® 101 NC010 Nylon 66  (Unverified Data**)
Zytel® 101 NC010 is a general purpose polyamide 66 resin for injection molding and extrusion.Information provided by DuPont Performance Polymers
Tensile Strength 110 MPa

@Temperature -40.0 °C
16000 psi

@Temperature -40.0 °F
ASTM D638
Solvay Specialty Polymers Amodel® ET-1000 HS Polyphthalamide (PPA) (Dry)
Amodel® ET-1000 HS is an impact modified, heat stabilized polyphthalamide (PPA) that exhibits exceptional impact strength and toughness. Like all Amodel® PPA resins, ET-1000 HS offers high fat..
Tensile Strength 110 MPa

@Temperature 23.0 °C
16000 psi

@Temperature 73.4 °F
ISO 527
BASF Ultradur B 4300 G4 20% Glass Filled PBT
Ultradur B4300 G4 is an easy flowing injection molding PBT with 20% glass fiber reinforcement for rigid, tough, and dimensionally stable parts.Applications: Program switches, thermostat parts, small..
Tensile Strength 110 MPa

@Strain 5.00 %,
Temperature 23.0 °C
16000 psi

@Strain 5.00 %,
Temperature 73.4 °F
50mm/min
BASF Ultramid® KR 4350 PA6/6T (Dry)
Description: For injection-molding and extrusion, exhibiting high toughness, strength and stiffness, low water absorption, high melting point (295 °C [563°F]). The mechanical properties remain con..
Tensile Strength 110 MPa

@Strain 1.00 %,
Temperature 60.0 °C
16000 psi

@Strain 1.00 %,
Temperature 140 °F
5mm/min
BASF Ultramid® KR 4355 G7 35% Glass Filled PA6/6T (Dry)
Description: 35% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties r..
Tensile Strength 110 MPa

@Treatment Temp. 150 °C,
Time 3.60e+6 sec
16000 psi

@Treatment Temp. 302 °F,
Time 1000 hour
new oil
BASF Ultrason® KR 4113 PESU with 10/10% Carbon Fibers/Graphite and 10% PTFE
Description: Compound based on PES with 30 % filler. The filler system, a mixture of carbon fibers, graphite and PTFE powder, considerably improves Ultrason’s tribological properties. In addition, ..
Tensile Strength 110 MPa

@Temperature -40.0 °C
16000 psi

@Temperature -40.0 °F
ASTM D638
Solvay Specialty Polymers Amodel® ET-1000 HS Polyphthalamide (PPA)  (Unverified Data**)
Amodel ET-1000 HS is an impact modified, heat stabilized polyphthalamide (PPA) that exhibits exceptional impact strength and toughness. Like all Amodel PPA resins, ET-1000 HS offers high fatigue str..