Polymer Property : Compressive Strength = 207 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Compressive Strength 207 MPa

@Temperature 216 °C
30000 psi

@Temperature 420 °F
Dry; ASTM D695
Park Electrochemical Nelcote® E-720 Epoxy Prepreg, 581 Quartz Reinforced
Nelcote® E-720 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-720 has a proven history in many demanding aerospac..
Compressive Strength 207 MPa

@Temperature 216 °C
30000 psi

@Temperature 420 °F
Dry, Autoclave with Post-Cure; ASTM D695
Park Electrochemical Nelcote® E-746 Epoxy Prepreg, 581 Quartz Reinforced
Nelcote® E-746 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-746 has a proven history in many demanding aerospac..
Compressive Strength 207 MPa

@Temperature 71.1 °C
30000 psi

@Temperature 160 °F
Dry; Autoclave, 50 psi, 90min; ASTM D695
Park Electrochemical Nelcote® F-529 Phenolic Prepreg, 7781 E-Glass Reinforced
Nelcote® F-529 is a non-halogenated phenolic resin designed specifically for use in aircraft and mass-transit interior laminate and sandwich panels. F-529 was formulated for applications requiring ..
Compressive Strength 207 MPa

@Temperature 23.0 °C
30000 psi

@Temperature 73.4 °F
JIS K7208
Mitsui AURUM® JCL3030 Thermoplastic Polyimide Resin, Amorphous, Wear/Friction Grade  (discontinued **)
AURUM® is an easy melt, processable and recyclable thermoplastic polyimide resin that provides continuous service temperatures to 465° F in its amorphous state and up to 550° F when annealed to i..
Compressive Strength 207 MPa

@Temperature 22.8 °C
30000 psi

@Temperature 73.0 °F
JIS K7208
Mitsui AURUM® JCL3030 Polyimide, Carbon Fiber Filled  (discontinued **)
AURUM JCL3030 is a high-performance polyimide for precision injection molded components and extruded products. A member of the AURUM family of advanced engineering resins, carbon fiber reinforced AU..
Compressive Strength 207 MPa

@Temperature 22.8 °C
30000 psi

@Temperature 73.0 °F
JIS K7208
Mitsui AURUM® JCN3030 Polyimide, Carbon Fiber Filled  (discontinued **)
AURUM JCN3030 is a high-performance polyimide for precision injection molded components and extruded products. A member of the AURUM family of advanced engineering resins, carbon fiber reinforced AU..