Polymer Property : Flexural Yield Strength = 9250 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Yield Strength | 63.7 - 92.2 MPa | 9250 - 13400 psi | Average value: 85.4 MPa Grade Count:6 |
| Overview of materials for PEN-PET This property data is a summary of similar materials in the MatWeb database for the category "PEN-PET". Each property range of values reported is minimum and maximum values of appropriate MatWeb ent.. |
|||
| Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
15 mm/min; ASTM D790 |
| LG Chemical AF342T ABS, Flame Retardant, High Impact Feature: Injection Molding, Flame Retardant, High ImpactApplication: Electric/Electronic Applications (TV, Monitor Housing) IT/OA deviceCAS No. 9003-56-9, 40039-93-8 and 1309-64-4Information provide.. |
|||
| Flexural Yield Strength | 63.7 MPa | 9250 psi | DIN 53455; ASTM D790 |
| Kolon NOPLA® KE531HC PEN-PET Copolyester NOPLA® is an advanced PEN-PET copolyester which can be used for bottle, sheet & injection molding applicationsUV protection & prolonged outdoor durability, enhanced gas barrier, outstanding impac.. |
|||
| Flexural Yield Strength | 63.7 MPa | 9250 psi | ASTM D790 |
| Iran Petrochemical (PCC) SH-0150 Acrylonitrile Butadiene Styrene SH - 0150 ABS extrusion grade has been formulated to provide excellent mechanical properties,extrusion stability, vacuum formability and chemical resistance. It is a high flow extrusion grade with h.. |
|||
| Flexural Yield Strength | 63.7 MPa @Temperature 23.0 °C |
9250 psi @Temperature 73.4 °F |
ASTM D790 |
| IRPC Polimaxx Porene KU650 Acrylonitrile Butadiene Styrene Applications:injection moldingautomotive parts such as instrument panels, console boxes, switches, automotive louvers, ectelectrical appliances |
|||
| Flexural Yield Strength | 63.7 MPa @Temperature 23.0 °C |
9250 psi @Temperature 73.4 °F |
ASTM D790 |
| IRPC Polimaxx Porene SP100 Acrylonitrile Butadiene Styrene Applications:injection moldinghelmetsautomotive |
|||
| Flexural Yield Strength | 63.7 MPa | 9250 psi | ASTM D790 |
| Lendell Parapet GR-00100 PMMA, High Impact |
|||
| Flexural Yield Strength | 63.7 MPa | 9250 psi | ASTM D790 |
| Samyang Triloy® 130 PC/PBT alloy Characteristics:Impact resistantChemical resistantDimensional stabilityProcessabilityGood flowApplications:Automotive bumperAutomotive outdoor handleAll information provided by Samyang |
|||
| Flexural Yield Strength | 63.7 MPa | 9250 psi | ASTM D790 |
| Samyang Trimma® SD6310H PMMA, Translucent High scratch resistance; stability against weak acids, strong acids, weak alkalis and inorganic salts.Applications: Laptop, Monitor Front Cover - for high flow, high gloss and high hardnessInformat.. |
|||
| Flexural Yield Strength | 63.7 MPa | 9250 psi | ASTM D790 |
| Cheng Yu Plastic ML849 Flame Retardant PC |
|||
| Flexural Yield Strength | 63.7 MPa | 9250 psi | ASTM D790 |
| Cheng Yu Plastic PP226 Flame Retardant Polypropylene, Medium Impact |
|||
| Flexural Yield Strength | 63.7 MPa | 9250 psi | ASTM D790 |
| Cheng Yu Plastic PP231H TALC 40 Polypropylene, 40% Talc, High Heat |
|||
| Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
ASTM D-790 |
| Bhansali Engineering Abstron IM-11B ABS Injection Molding Grade High Impact Strength, Medium Flow, High Fatigue ResistanceInformation provided by Bhansali |
|||
| Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
| Bhansali Engineering Abstron IM17A TT ABS Injection Molding Grade High Flow, Medium ImpactInformation provided by Bhansali |
|||
| Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
ASTM D790 |
| Bhansali Engineering Abstron MIF-45 ABS Injection Molding Grade High Impact, Medium, High Flow, General PurposeInformation provided by Bhansali |
|||
| Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
| Bhansali Engineering Abstron SE45I Extrusion ABS Very High Impact, Low Flow, High Rigidity and Sheet/Pipe/Profile applicationInformation provided by Bhansali |
|||
| Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
| Bhansali Engineering Abstron IM17V ABS Injection Molding Grade Super High Gloss, Medium ImpactInformation provided by Bhansali |
|||
| Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
| Bhansali Engineering Abstron IM21G ABS Injection Molding Grade Super High Gloss, Medium ImpactInformation provided by Bhansali |
|||
| Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
ASTM D790 |
| Bhansali Engineering Abstron MIF-35 ABS Injection Molding Grade High Impact, Medium, High Flow, General PurposeInformation provided by Bhansali |
|||
| Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
| Bhansali Engineering Abstron MIF45EP ABS Injection Molding Grade Electroplating, High FlowInformation provided by Bhansali |
|||
| Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
| Bhansali Engineering Abstron SE45I Extrusion ABS Very High Impact, Low Flow, High Rigidity and Sheet/Pipe/Profile applicationInformation provided by Bhansali |
|||
| Flexural Yield Strength | 63.7 MPa | 9250 psi | ASTM D790 |
| Cheng Yu Plastic IPS601 Flame Retardant HIPS |
|||
| Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
| Bhansali Engineering Abstron HI40I ABS Injection Molding Grade Automotive applications -Super High Impact , High Rigidity, PaintableInformation provided by Bhansali |
|||
| Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
ASTM D-790 |
| Bhansali Engineering Abstron IM-11B ABS Injection Molding Grade High Impact Strength, Medium Flow, High Fatigue ResistanceInformation provided by Bhansali |
|||
| Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
| Bhansali Engineering Abstron IM17V ABS Injection Molding Grade Super High Gloss, Medium ImpactInformation provided by Bhansali |
|||
| Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
| Bhansali Engineering Abstron MIF45EP ABS Injection Molding Grade Electroplating, High FlowInformation provided by Bhansali |
|||
| Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
| Bhansali Engineering Abstron IM17A TT ABS Injection Molding Grade High Flow, Medium ImpactInformation provided by Bhansali |
|||
| Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
ASTM D790 |
| Bhansali Engineering Abstron MIF-45 ABS Injection Molding Grade High Impact, Medium, High Flow, General PurposeInformation provided by Bhansali |
|||
| Flexural Yield Strength | 63.7 MPa | 9250 psi | ASTM D790 |
| Cheng Yu Plastic IPS620BK Electric Conducting HIPS, Injection |
|||
| Flexural Yield Strength | 63.7 MPa | 9250 psi | ASTM D790 |
| Cheng Yu Plastic IPS666N Electric Resisting HIPS |
|||