Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 56.9 MPa @Thickness 3.20 mm |
8250 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
LG Chemical RX710 ABS, High Impact, Chemical Resistance to HCFC Feature: Injection Molding, Chemical Resistance to HCFC, High ImpactApplication: Refrigerator Dispensor & HomebarCAS No. 9003-56-9Information provided by LG Chemical |
|||
Flexural Yield Strength | 56.9 MPa @Thickness 3.20 mm |
8250 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
LG Chemical SH610S ABS, Excellent Surface, High Impact Feature: Extrusion Molding, Excellent Surface, High ImpactApplication: Bag, miscellaneousCAS No. 9003-56-9Information provided by LG Chemical |
|||
Flexural Yield Strength | 56.9 MPa | 8250 psi | ASTM-D790 |
Ineos ABS Triax® 3050 ABS/Nylon Alloy, Injection Molding Grade (Conditioned) Triax® 3050 resin is an ABS (Acrylonitrile Butadiene Styrene)/Nylon 6 alloy for injection molding. It is a semicrystalline thermoplastic with improved stability to light exposure, excellent proce.. |
|||
Flexural Yield Strength | 56.9 MPa @Thickness 6.40 mm |
8250 psi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron AN-450 Flame Retardant ABS Grade Information provided by Bhansali |
|||
Flexural Yield Strength | 56.9 MPa @Thickness 6.40 mm |
8250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Abstron AN450M Flame Retardant ABS Flame Retardant- V0 at 3.0mm (UL 94 certified)Information provided by Bhansali |
|||
Flexural Yield Strength | 56.9 MPa @Thickness 6.40 mm |
8250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Abstron SE32H Extrusion ABS Very High Impact, Better Flow and Sheet/Pipe/Profile applicationInformation provided by Bhansali |
|||
Flexural Yield Strength | 56.9 MPa @Thickness 6.40 mm |
8250 psi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron AN-450 EVM Flame Retardant ABS Grade Information provided by Bhansali |
|||
Flexural Yield Strength | 56.9 MPa @Thickness 6.40 mm |
8250 psi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron AN-450 Flame Retardant ABS Grade Information provided by Bhansali |
|||
Flexural Yield Strength | 56.9 MPa @Thickness 6.40 mm |
8250 psi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron AN-450 EVM Flame Retardant ABS Grade Information provided by Bhansali |
|||
Flexural Yield Strength | 56.9 MPa @Thickness 6.40 mm |
8250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Abstron AN450M Flame Retardant ABS Flame Retardant- V0 at 3.0mm (UL 94 certified)Information provided by Bhansali |
|||
Flexural Yield Strength | 56.9 MPa @Thickness 6.40 mm |
8250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Abstron SE32H Extrusion ABS Very High Impact, Better Flow and Sheet/Pipe/Profile applicationInformation provided by Bhansali |