Polymer Property : Flexural Yield Strength = 7250 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Yield Strength 50.0 MPa

@Temperature 90.0 °C
7250 psi

@Temperature 194 °F
ISO 178, ASTM D790
Nilit Nilitop BT G2 FR C3 is a 10% Glass Fiber Reinforced, Flame Retardant PBT
Description: Nilitop BT G2 FR C3 is a 10% glass fiber reinforced, flame retardant PBT with halogens. The flame retardant does not contain PBB and PBDE, so it is compliant with the WEEE directive. It..
Flexural Yield Strength 50.0 MPa
7250 psi
2 mm/min; ISO 178
SABIC Innovative Plastics GELOY FXW710SK ASA
General purpose injection molding ASA with Visual Fx sparkle effect.
Flexural Yield Strength 50.0 MPa
7250 psi
ASTM D790
RedEye On Demand PC/ABS for FDM Rapid Prototyping
This thermoplastic polymer blend combines PC (Polycarbonate) and ABS (Acrylonitrile Butadiene Styrene) to produce an industrial material with a lot to offer. It combines the strength of PC with the ..
Flexural Yield Strength 50.0 - 50.0 MPa

@Temperature 90.0 - 90.0 °C
7250 - 7250 psi

@Temperature 194 - 194 °F
Average value: 50.0 MPa Grade Count:1
Overview of materials for Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled".Specific grades with glass content between 5% ..
Flexural Yield Strength 50.0 MPa
7250 psi
2 mm/min; ISO 178
SABIC Innovative Plastics GELOY CR7020 ASA (Europe-Africa-Middle East)
GELOY CR7020 is a profile extrusion and co-extrusion grade, blend of ASA/SAN. In co-extrusion it can be used over CYCOLAC, PVC or other compatible polymers.
Flexural Yield Strength 50.0 MPa
7250 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Geloy CR7520 ASA (Europe-Africa-Middle East)
Geloy CR7520 is a general purpose injection moulding grade, blend of ASA/SAN. It can be positioned for outside parts in various markets, such as telecommunication, transportation, B&C, lighting and ..
Flexural Yield Strength 50.0 MPa

@Temperature 90.0 °C
7250 psi

@Temperature 194 °F
ISO 178, ASTM D790
Nilit Nilamid B FR HF Unfilled, Flame Retardant, Halogen and Red Phosphorous Free PA6
Description: Nilamid B FR HF is an unfilled, flame retardant NYLON 6 with excellent flow characteristics, outstanding elongation and impact strength and a good thermal performance. Because of its ex..
Flexural Yield Strength 50.0 MPa
7250 psi
DIN 53452
Ineos Nova S-2200 Medium Impact Compact Polystyrene  (discontinued **)
Medium impact easy flowing polystyrene, designed for injection molding applications with short cycle times and for complicated technical parts. The product has a high stiffness and an excellent the..
Flexural Yield Strength 50.0 MPa
7250 psi
DIN 53452
Ineos Nova S-4200 Medium Impact Compact Polystyrene  (discontinued **)
Medium impact polystyrene which combines excellent flow characteristics with a good dimensional stability under heat and a high stiffness. This grade is designed for injection molding of technical..
Flexural Yield Strength 50.0 MPa
7250 psi
DIN 53452
Ineos Nova S-4400 High Impact Compact Polystyrene  (discontinued **)
Impact polystyrene which combines excellent flow characteristics with a good dimensional stability under heat and a high stiffness. This grade is designed for injection molding of technical parts o..
Flexural Yield Strength 50.0 - 131 MPa
7250 - 19000 psi
Average value: 81.2 MPa Grade Count:108
Overview of materials for Polycarbonate/PET Polyester Blend
This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/PET Polyester Blend". Each property range of values reported is minimum and maximum values..
Flexural Yield Strength 50.0 - 190 MPa
7250 - 27500 psi
Average value: 114 MPa Grade Count:44
Overview of materials for Nylon 6, 30% Mineral Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Mineral Filled". Specific grades with primary filler content between 25% and 34% are includ..
Flexural Yield Strength 50.0 - 250 MPa
7250 - 36300 psi
Average value: 117 MPa Grade Count:50
Overview of materials for Nylon 6, 40% Mineral Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 40% Mineral Filled". Each property range of values reported is minimum and maximum values of ap..
Flexural Yield Strength 50.0 - 261 MPa
7250 - 37800 psi
Average value: 166 MPa Grade Count:111
Overview of materials for Nylon 6, Glass/Mineral Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass/Mineral Reinforced". Each property range of values reported is minimum and maximum values..
Flexural Yield Strength 50.0 - 190 MPa
7250 - 27600 psi
Average value: 87.1 MPa Grade Count:4
Overview of materials for Nylon, Amorphous Transparent Alloy
This property data is a summary of similar materials in the MatWeb database for the category "Nylon, Amorphous Transparent Alloy". Each property range of values reported is minimum and maximum value..
Flexural Yield Strength 50.0 MPa
7250 psi
at 3.5% strain; 6% strain at break; ISO 178
FKuR Kunststoff Bio-Flex® S 6540 Compostable PLA Blend
The BIO-FLEX® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEX® does not contain any sta..
Flexural Yield Strength 50.0 MPa
7250 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Noryl RF1132 PPE+PP
PPE+PP blend for high frequency applications. Good heat resistance and low DK.This data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength 50.0 MPa
7250 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP Thermocomp M10009A PP (Europe-Africa-Middle East)
LNP* STARFLAM* M10009A is a compound based on Polypropylene resin, containing Flame Retardant. Added features include : Flame Retardant.This data was supplied by SABIC-IP for the Europe-Africa-Middl..
Flexural Yield Strength 50.0 MPa
7250 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP WH0420A_GY5A749 PBT
4.2 specific gravity, PBT, gray
Flexural Yield Strength 50.0 MPa
7250 psi
2 mm/min; ISO 178
SABIC Innovative Plastics NORYL PPX PPX7110 PPE+PP (Europe-Africa-Middle East)
PPX7110 is an alloy of PP and PPO, providing high impact and good heat resistance. Generic identification acc. ISO11469: >PP+PPE+PS-I
Flexural Yield Strength 50.0 MPa
7250 psi
ISO 178
Solvay Technyl® A 205F Nylon 66, EH50
Unreinforced polyamide 66, high fluidity, fast cycling grade, for injection molding.Technyl A 205F offers two main advantages: excellent filling qualities and UL 94 V2 under 0.4 mm. It is particula..
Flexural Yield Strength 50.0 MPa
7250 psi
2 mm/min; ISO 178
Eurostar Starflam M10009A PP, Flame Retardant, Injection Molding
Starflam M10009A is an Unfilled Flame Retardant Polypropylene (Homo) Injection Molding ResinInformation provided by Eurostar.
Flexural Yield Strength 50.0 - 303 MPa
7250 - 44000 psi
Average value: 115 MPa Grade Count:108
Overview of materials for Nylon 66, PTFE Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, PTFE Filled". Each property range of values reported is minimum and maximum values of appropri..
Flexural Yield Strength 50.0 - 100 MPa
7250 - 14500 psi
Average value: 73.8 MPa Grade Count:25
Overview of materials for Polybutylene Terephthalate (PBT), PTFE Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), PTFE Filled". Each property range of values reported is minimum and ma..
Flexural Yield Strength 50.0 MPa
7250 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Geloy FXW710SK ASA/SAN (Europe-Africa-Middle East)
GELOY FXW710SK is an ASA/SAN injection moulding grade. It is suitable for those applications that require sparkle colour effects.This data was supplied by SABIC-IP for the Europe-Africa-Middle East ..
Flexural Yield Strength 50.0 - 241 MPa
7250 - 35000 psi
Average value: 143 MPa Grade Count:123
Overview of materials for Polypropylene with 40% Glass Fiber Filler
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Glass Fiber Filler". Specific grades with glass content between 35% and 44% are i..
Copyright © lookpolymers.com All Rights Reserved