Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 42.0 MPa | 6090 psi | ASTM D790 |
North Wood Plastics Polypropylene with 60% Wood Fiber, Extrusion Grade Data provided by North Wood Plastics, Inc. |
|||
Flexural Yield Strength | 42.0 MPa | 6090 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Faradex KS003AI Acetal Copolymer (Europe-Africa-Middle East) LNP* FARADEX* KS003AI is a compound based on Acetal Copolymer resin containing Stainless Steel Fiber. Added features include; EMI/RFI Shielding, Electrically Conductive.This data was supplied by SAB.. |
|||
Flexural Yield Strength | 42.0 - 42.0 MPa @Temperature 100 - 100 °C |
6090 - 6090 psi @Temperature 212 - 212 °F |
Average value: 42.0 MPa Grade Count:1 |
Overview of materials for Polyphthalamide (PPA), High Impact This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, High Impact". Each property range of values reported is minimum and maximum values of a.. |
|||
Flexural Yield Strength | 42.0 - 116 MPa | 6090 - 16800 psi | Average value: 79.5 MPa Grade Count:15 |
Overview of materials for Acetal Copolymer, Steel Filled This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Steel Filled". Each property range of values reported is minimum and maximum values of.. |
|||
Flexural Yield Strength | 42.0 - 260 MPa @Temperature -40.0 - 150 °C |
6090 - 37700 psi @Temperature -40.0 - 302 °F |
Average value: 109 MPa Grade Count:2 |
Overview of materials for Liquid Crystal Polymer (LCP), Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), Mineral Filled". Each property range of values reported is minimum and max.. |
|||
Flexural Yield Strength | 42.0 - 260 MPa @Thickness 0.800 - 3.17 mm |
6090 - 37700 psi @Thickness 0.0315 - 0.125 in |
Average value: 109 MPa Grade Count:2 |
Overview of materials for Liquid Crystal Polymer (LCP), Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), Mineral Filled". Each property range of values reported is minimum and max.. |
|||
Flexural Yield Strength | 42.0 MPa | 6090 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON CD0001 PS LNP* STAT-KON* CD000I is a compound based on Polystyrene resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact. |
|||
Flexural Yield Strength | 42.0 MPa | 6090 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON CD000I PS LNP* Stat-kon* CD000I is a compound based on Polystyrene resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact. |
|||
Flexural Yield Strength | 42.0 MPa | 6090 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermocomp MB006SU PP (Europe-Africa-Middle East) LNP* THERMOCOMP* MB006SU is a compound based on Polypropylene resin containing Glass Bead. Added features include: Heat Stabilized, UV-Stabilized.This data was supplied by SABIC-IP for the Europe-Af.. |
|||
Flexural Yield Strength | 42.0 MPa | 6090 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL HIPS3190 HIPS Complies with FDA Regulation 21 CFR 177.1640 for rubber modified polystyrene. HB rating from 0.062-0.125"" pending. Natural only. |
|||
Flexural Yield Strength | 42.0 MPa | 6090 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP SH1100A PA12 LNP* Thermocomp* SH1100A is a Nylon 12, High Specificy Gravity compound containing proprietary fillers. |
|||
Flexural Yield Strength | 42.0 MPa | 6090 psi | 2 mm/min; ISO 178 |
Eurostar Starpylen MB006SU PP, Glass Bead Filled, Injection Molding Resin Starpylen MB006SU is a Glass Bead Reinforced Polypropylene Injection Molding ResinInformation provided by Eurostar. |
|||
Flexural Yield Strength | 42.0 MPa | 6090 psi | ASTM D790 |
3D Systems DuraForm® EX Impact-Resistant Plastic for SLS® Systems This impact-resistant plastic offers the toughness of injection-molded polypropylene and ABS and is suitable for Rapid Manufacturing. For use with all Sinterstation® Pro and Sinterstation HiQ™ ser.. |