Polymer Property : Flexural Yield Strength = 5970 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	41.2 MPa @Thickness 3.20 mm	5970 psi @Thickness 0.126 in	15mm/min; ASTM D790
LG Chemical HIPS 403AF PS, Flame Retardant Description: Injection Molding, PS, Flame RetardantApplication: Electric Parts Requiring Flame RetardancyCAS: 9003-55-8, 21850-44-2 and 1309-64-4Information provided by LG Chemical
Flexural Yield Strength	41.2 MPa @Thickness 6.40 mm	5970 psi @Thickness 0.252 in	30mm/min; ASTM D790
LG Chemical LUPOL HI5204G PP+MF20%, High Impact Description: Injection Molding, PP+MF20%, High Impact, Good WeatherabilityApplication: Automotive Interior PartsCAS: 9003-07-0, 26221-73-8 and 14807-96-6Information provided by LG Chemical
Flexural Yield Strength	41.2 MPa @Thickness 6.40 mm	5970 psi @Thickness 0.252 in	30mm/min; ASTM D790
LG Chemical LUPOL HM5204 PP+MF20%, High Impact Description: Injection Molding, PP+MF20%, High Impact, Good WeatherabilityApplication: Automotive Interior PartsCAS: 9003-07-0, 9010-79-1 and 14807-96-6Information provided by LG Chemical
Flexural Yield Strength	41.2 MPa	5970 psi	ASTM D790
IRPC Polimaxx Polene 1196NN Polypropylene Compound CHARACTERISTICS: POLYPROPYLENE HOMOPOLYMER UNREINFORCED, CONTAIN FLAME RETARDANT, UL 94 V-2 APPROVAL, HIGH IMPACT STRENGTHAPPLICATIONS: INJECTION MOLDING FOR ELECTRICAL APPLIANCES
Flexural Yield Strength	41.2 MPa @Temperature 300 °C	5970 psi @Temperature 572 °F	ASTM D790
UBE UPIMOL® S High Heat Polyimide Shape Description: Ube's UPIMOL is an exceptionally heat-resistant polyimide Shape. This product has the same molecular structure as UPILEX, an ultra-high heat-resistant polyimide film developed by Ub..
Flexural Yield Strength	41.2 MPa	5970 psi	ASTM D790
Diapolyacrylate Acrypet® IR H70 Impact Modified PMMA Acrypet® is a registered trade mark of Diapolyacrylate Company Limited. Information provided by Dayson Polymers.
Flexural Yield Strength	41.2 - 105 MPa	5970 - 15200 psi	Average value: 69.8 MPa Grade Count:110
Overview of materials for Acrylic, Impact Modified, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Impact Modified, Molded". Each property range of values reported is minimum and maximum values ..