Polymer Property : Flexural Yield Strength = 59.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	59.0 MPa	8560 psi	ASTM D790
Ineos Nova 4211 Medium Impact Polystyrene (discontinued **) Excellent balance of properties, USP Class VIApplications: Consumer electronics, Injection molding applicationsProperties were determined on injection molded specimens at 23°C and 50% R.H. unless o..
Flexural Yield Strength	59.0 - 205 MPa	8560 - 29700 psi	Average value: 112 MPa Grade Count:11
Overview of materials for Nylon 6, Mineral Reinforced, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Mineral Reinforced, Impact Grade". Each property range of values reported is minimum and maximu..
Flexural Yield Strength	59.0 MPa	8560 psi	ASTM D790
Plenco 5440 Black General Purpose Phenolic Molding Compound (discontinued **) Plaslok 5440 is the replacement material for the former Union Carbide BMRS-5440. It is a two-stage, phenolic molding compound that has been successfully formulated to accommodate a very wide range ..
Flexural Yield Strength	59.0 MPa	8560 psi	ASTM-D790
Ineos ABS LustranÂ® 266 ABS, Transparent Grade LustranÂ® ABS 266 resin is a clear injection molding grade of ABS (acrylonitrile butadiene styrene). This transparent, general-purpose grade provides clarity and toughness with ease of processing...
Flexural Yield Strength	59.0 MPa	8560 psi
Kuraray HYBRARÂ® A1 Thermoplastic Rubber-ABS Blend HYBRARÂ® is another in the series of new high performance thermoplastic rubbers developed by KURARAY using their unique isoprene technology. HYBRARÂ® is a special thermoplastic rubber which exhi..
Flexural Yield Strength	59.0 MPa	8560 psi	ASTM D790
Hannam Chemical Hanalac 740 ABS, Super High Impact Grade Superior impact strength, even at low temperature. Applications: helmets, shoe heels, bobbins, roller skates, bags, pipes, radiator grills, auto parts, appliance wheels.
Flexural Yield Strength	59.0 MPa	8560 psi	ASTM D790
Hannam Chemical Hanalac 770 ABS, Extrusion Grade FDA Approved. Excellent mechanical strength, high rigidity, and high impact strength. Good thermoformability. Applications: Refrigerators liners, bathtubs, automobile interiors, portable bags, n..
Flexural Yield Strength	59.0 MPa	8560 psi	ASTM D790
Hannam Chemical Hanalac HFA-700 ABS
Flexural Yield Strength	59.0 MPa	8560 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL WCV072 PPE+PP (Asia Pacific) Flexible, halogen free mPPE extrusion grade material for applications such as automotive wire insulation. Low specific gravity with good flame retardant and very good scrape abrasion resistance. De..
Flexural Yield Strength	59.0 MPa	8560 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL WCV072 PPE+PP (Europe-Africa-Middle East) Flexible, halogen free mPPE extrusion grade material for applications such as automotive wire insulation. Low specific gravity with good flame retardant and very good scrape abrasion resistance. De..
Flexural Yield Strength	59.0 MPa	8560 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP KL004L Acetal Copoly (Asia Pacific) LNP* Lubricomp* KL004L is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
Flexural Yield Strength	59.0 MPa	8560 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-LOY A3000 ABS (Asia Pacific) LNP STAT-LOY A3000 is a compound based on Acrylonitrile butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistatic. Also known as: STAT-LOY A
Flexural Yield Strength	59.0 MPa	8560 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL WCV072 PPE+PP Flexible, halogen free mPPE extrusion grade material for applications such as automotive wire insulation. Low specific gravity with good flame retardant and very good scrape abrasion resistance. De..
Flexural Yield Strength	59.0 MPa	8560 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-LOY P3000U PA 6 (Europe-Africa-Middle East) LNP* Stat-loy* P3000U is a compound based on PA 6 resin. Added features include; Antistatic, UV - Stabilized.
Flexural Yield Strength	59.0 MPa	8560 psi	ASTM D790
Chem Polymer Chemlon 280 Nylon 6, High Impact A highly impact modified nylon 6 exhibiting excellent toughness and flexibility.Data provided by the manufacturer, Chem Polymer.
Flexural Yield Strength	59.0 MPa	8560 psi	ASTM D790
Plaslok 5440 Black General Purpose Phenolic Molding Compound (discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 5440 is the replacement material for ..