Polymer Property : Flexural Yield Strength = 45.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	45.0 - 172 MPa	6530 - 25000 psi	Average value: 75.2 MPa Grade Count:34
Overview of materials for Polybutylene Terephthalate (PBT), Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Impact Grade". Each property range of values reported is minimum and m..
Flexural Yield Strength	45.0 - 350 MPa @Temperature 120 - 275 °C	6530 - 50800 psi @Temperature 248 - 527 °F	Average value: 151 MPa Grade Count:11
Overview of materials for Polyetheretherketone, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, Carbon Fiber Filled". Each property range of values reported is minimum and maximu..
Flexural Yield Strength	45.0 MPa	6530 psi	DIN 53452
Ineos Nova S-6600 High Impact Compact Polystyrene (discontinued **) High impact polystyrene which is very easy processed in extension and thermoforming processes. Typical applications are packaging of food stuffs like Yot beakers but technical parts and extruded pr..
Flexural Yield Strength	45.0 - 52.0 MPa	6530 - 7540 psi	ASTM D790
Solvay Specialty Polymers Hylar® 460 PVDF Polyvinylidene Fluoride (discontinued **) Data provided by the manufacturer.Hylar® polymers have the characteristic stability of fluoropolymers combined with a unique polarity that influences its solubility and electrical properties. In a..
Flexural Yield Strength	45.0 - 380 MPa	6530 - 55100 psi	Average value: 285 MPa Grade Count:18
Overview of materials for Nylon 66/6, 40% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 40% Glass Fiber Reinforced". Specific grades with glass content between 35% and 44% are incl..
Flexural Yield Strength	45.0 MPa	6530 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Thermocomp 4X08423 LNP* Thermocomp* 4X08423 is a compound based on Perfluoroalkoxy Polymer (PFA) containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength	45.0 MPa	6530 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Thermocomp MX96070 PP (Europe-Africa-Middle East) LNP* STARFLAM* MX96070 is a compound based on Polypropylene resin containing Flame Retardant. Added features include: Flame Retardant.This data was supplied by SABIC-IP for the Europe-Africa-Middl..
Flexural Yield Strength	45.0 MPa	6530 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP YF003S Polyester Elastomer (Europe-Africa-Middle East) LNP* THERMOCOMP* YF003S is a compound based on Polyester Elastomer containing Glass Fiber. Added features include; Heat Stabilized.
Flexural Yield Strength	45.0 MPa	6530 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL PX1185 PPE+HIPS (Europe-Africa-Middle East) NORYL PX1185 is a special NORYL grade developed for extrusion of automotive trims. NORYL PX1185 offers high heat resistance and good impact performance.
Flexural Yield Strength	45.0 MPa	6530 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-KON KD000EI Acetal Copolymer (Europe-Africa-Middle East) LNP* Stat-Kon* KD000EI is a compound based on Acetal Copolymer resin containing Carbon Powder. Added features include: Electrically Conductive, Impact Modified.
Flexural Yield Strength	45.0 MPa	6530 psi	ASTM D790
Tipco Tipcolene® FPC 40 - 40% Calcium Carbonate Reinforced Polypropylene Homopolymer 40% Calcium Carbonate Filled PP HomopolymerApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd., India.
Flexural Yield Strength	45.0 MPa	6530 psi	ASTM D790
Tipco Tipcolene® FPT 20 FR VO PPC - UL94-V0 Flame Retardant, 20% Talc Polypropylene Copolymer 20% Talc Reinforced PP CopolymerApplications: Electrical & AppliancesProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd., India.
Flexural Yield Strength	45.0 MPa	6530 psi	2 mm/min; ISO 178
Eurostar Starpylen MZ006S PP, Glass Fiber Filled, Injection Molded Starpylen MZ006S is a Glass fiber Reinforced, Polypropylene Injection Molding Resin heat stabilized (also known as Starpylen WT 30GF S3)Information provided by Eurostar.
Flexural Yield Strength	45.0 MPa	6530 psi	ASTM D790
Chem Polymer Durlex 709 IH PBT, Impact Modified A highly impact modified PBT exhibiting excellent toughness and processability.Data provided by the manufacturer, Chem Polymer.
Flexural Yield Strength	45.0 MPa	6530 psi	ASTM D790
Ineos Nova 5620 High Impact Polystyrene (discontinued **) High heat resistance, Good balance of toughness and rigidityApplications: Food service itemProperties were determined on injection molded specimens at 23°C and 50% R.H. unless otherwise specified.I..
Flexural Yield Strength	45.0 - 240 MPa @Temperature -40.0 - 90.0 °C	6530 - 34800 psi @Temperature -40.0 - 194 °F	Average value: 116 MPa Grade Count:4
Overview of materials for Nylon 6, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Glass Fiber Filled".Specific grades with glass content between 15% and 24% are included. Ea..
Flexural Yield Strength	45.0 MPa	6530 psi	ASTM D790
E-Polymers TEKAMID® TB120ST Super Tough PA6, DAM Super ToughnessInformation provided by E-Polymers Co. Ltd.