Polymer Property : Flexural Yield Strength = 35.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Yield Strength 35.0 MPa

@Temperature 90.0 °C
5080 psi

@Temperature 194 °F
ISO 178, ASTM D790
Nilit Nilitop BT FR C3 Unfilled, Flame Retardant PBT
Description: Nilitop BT FR C3 is an unfilled, flame retardant PBT with halogens. The flame retardant does not contain PBB and PBDE, so it is compliant with the WEEE directive.Key characteristics: Go..
Flexural Yield Strength 35.0 MPa
5080 psi
ASTM D790
North Wood Plastics HDPE with 40% Wood Fiber
Data provided by North Wood Plastics, Inc.
Flexural Yield Strength 35.0 - 35.0 MPa

@Temperature 90.0 - 90.0 °C
5080 - 5080 psi

@Temperature 194 - 194 °F
Average value: 35.0 MPa Grade Count:1
Overview of materials for Polybutylene Terephthalate (PBT), Flame Retardant
This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Flame Retardant". Each property range of values reported is minimum an..
Flexural Yield Strength 35.0 MPa

@Temperature 90.0 °C
5080 psi

@Temperature 194 °F
ISO 178, ASTM D790
Nilit Nilamid A3 N H2 Nucleated, Heat Stabilized Nylon 66
Description: Nilamid A3 N H2 is a nucleated, heat stabilized NYLON 66 with excellent flow characteristics and very fast cycle time. It is widely used throughout many industries for mass production a..
Flexural Yield Strength 35.0 MPa
5080 psi
DIN 53452
Ineos Nova S-4600 High Impact Compact Polystyrene  (discontinued **)
High impact polystyrene with excellent flow characteristics, a very high toughness and a high elongation. Main application are injection molding of technical parts and housings. For injection mold..
Flexural Yield Strength <= 35.0 MPa
<= 5080 psi
ASTM D790
3M Dyneon™ CC144/S PTFE, 40% Bronze Filled  (discontinued **)
Product Form: Brown, non-pelletized powder. Applications include bearings, rider rings, and piston rings.Data provided by Dyneon.
Flexural Yield Strength 35.0 - 35.0 MPa

@Temperature 90.0 - 90.0 °C
5080 - 5080 psi

@Temperature 194 - 194 °F
Average value: 35.0 MPa Grade Count:1
Overview of materials for Nylon 66, Heat Stabilized
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Heat Stabilized". Each property range of values reported is minimum and maximum values of appr..
Flexural Yield Strength 35.0 MPa
5080 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-KON FX91304 PE
LNP* STAT-KON* FX91304 is a compound based on Polyethylene resin containing Proprietary Filler(s). Added feature of this grade is: Electrically Conductive.
Flexural Yield Strength 35.0 MPa
5080 psi
ASTM D790
Tipco Tipcolene® NPI 200 IN - 25% Talc/Mineral Reinforced Polypropylene Copolymer with Very High Flow, Stiffness & Impact Strength
20% Mineral Reinforced, Very High Stiffness & Very High Impact PP CopolymerApplications: Automotive DashboardsProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries ..
Flexural Yield Strength 35.0 MPa
5080 psi
2 mm/min; ISO 178
Eurostar Starpylen MX06023 PP, 20% Milled Glass Fiber Filled, Injection Molded
Starpylen MX06023 is a 20% Milled Glass Fiber Reinforced Polypropylene Injection Molding ResinInformation provided by Eurostar.
Flexural Yield Strength 35.0 - 138 MPa
5080 - 20000 psi
Average value: 110 MPa Grade Count:15
Overview of materials for Nylon 66, Nucleated
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Nucleated". Each property range of values reported is minimum and maximum values of appropriat..
Flexural Yield Strength 35.0 MPa
5080 psi
ASTM D790