Polymer Property : Flexural Yield Strength = 29700 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	205 MPa	29700 psi	1.3 mm/min, 50 mm span; ASTM D790
Ovation Polymers UTTAP QU HT530 GF Nylon, 30% Glass Reinforced Glass reinforced (30 %) - High Temperature Polyamide Alloy, excellent chemical and electrical resistance, high stiffness, modulus and HDT. *All properties are measured after 48 hours of conditioning..
Flexural Yield Strength	205 MPa	29700 psi	ASTM D790
Solvay Specialty Polymers Ryton® R-4-230BL Polyphenylene Sulfide Compound (Unverified Data**) Black Polyphenylene Sulfide CompoundRyton® R-4-230BL is an advanced 40% fiberglass reinforced polyphenylene sulfide compound which provides reduced flash and improved processability compared to oth..
Flexural Yield Strength	205 MPa	29700 psi	ASTM D790
Firestone CG430-001 Nylon 6, 30% Fiberglass Filled Natural color. Heat stabilized. Fiber size is 4 mm length and 14 Âµm diameter.Information provided by Firestone
Flexural Yield Strength	205 MPa	29700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® 420 PBT (Europe-Africa-Middle East) VALOX 420 is a 30% glass fiber reinforced PBT injection moulding resin with excellent mechanical and thermal properties. Applications: appliance handles, spotlights, electric motors.
Flexural Yield Strength	205 MPa	29700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® 553 PBT (Europe-Africa-Middle East) VALOX 553 is a 30% glass fibre reinforced, flame retardant PBT+PC blend with good warpage characteristics. Applications: appliance handles, spotlights, electric motors, pumphousings.
Flexural Yield Strength	205 MPa	29700 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP OCF62 PPS - Branched LNP* THERMOCOMP* OCF62 is a compound based on PPS-Branched resin containing 10% Carbon Fiber, 30% Glass Fiber. Added feature of this material includes: Easy Molding
Flexural Yield Strength	205 MPa	29700 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP OCF62E PPS - Branched LNP* THERMOCOMP* OCF62E is a compound based on PPS-Branched resin containing 10% Carbon Fiber, 30% Glass Fiber. Added feature of this material includes: Easy Molding
Flexural Yield Strength	205 MPa	29700 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® 830 PBT (Europe-Africa-Middle East) VALOX 830 is a 30% glass fibre reinforced PBT+PET blend with excellent surface finish. Applications: hot air gun housing assemblies, industrial glue guns, appliance housings and handles.
Flexural Yield Strength	205 MPa	29700 psi	ASTM D790
Chevron Phillips Xtel® XK2140 Polyphenylene Sulfide Alloy (discontinued **) Black Polyphenylene Sulfide AlloyXtel™ XK2140 is a high performance, glass fiber reinforced, PPS-based alloy developed to provide excellent mechanical strength and electrical properties along with ..
Flexural Yield Strength	205 MPa	29700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-KON QEP35M PA6.10 LNP STAT-KON QEP35M is a compound based on Nylon 6/10 resin containing 25% Milled Carbon Fiber, 15% PTFE/Silicone. Added features of this grade include: Electrically Conductive, Wear Resistant.