Polymer Property : Flexural Yield Strength = 2900 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	20.0 MPa	2900 psi	ASTM D790
Multibase Multi-Pro® 3011 CHI Polypropylene Calcium Carbonate Filler, 30% by weight.Forms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase
Flexural Yield Strength	20.0 MPa	2900 psi	1.3 mm/min, 50 mm span; ASTM D790
Ovation Polymers Opnyl OP6MT254 Nylon 6 Nylon 6 – Mighty Tough plasticized extrusion grade for tubing/profile applications. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are p..
Flexural Yield Strength	20.0 MPa	2900 psi	ASTM D580
Protective Coating PC-7® Epoxy Paste PC-7® is a tough job Epoxy formulation developed for maximum bonding power. Components A (grey) and B (black), when mixed, react to form a bond of good strength. PC-7® formulation provides exten..
Flexural Yield Strength	20.0 MPa	2900 psi	ASTM D580
Protective Coating PC-SuperEpoxy™ Translucent Epoxy Putty PC-SUPEREPOXY™ is a non-drip, thixotropic, translucent paste with unlimited uses in bonding, sealing, and as a filler for most materials. Unlike conventional liquid epoxies, PC-SUPEREPOXY™ can be..
Flexural Yield Strength	20.0 - 180 MPa	2900 - 26100 psi	Average value: 44.5 MPa Grade Count:58
Overview of materials for Polypropylene, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Molded". Each property range of values reported is minimum and maximum values of appropri..
Flexural Yield Strength	20.0 - 88.0 MPa	2900 - 12800 psi	Average value: 46.6 MPa Grade Count:74
Overview of materials for Polypropylene with 30% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Talc Filler". Specific grades with primary filler content between 25% and 34% are..
Flexural Yield Strength	20.0 - 51.0 MPa	2900 - 7400 psi	Average value: 32.2 MPa Grade Count:28
Overview of materials for Polypropylene with 20% Mica Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Mica Filler". Specific grades with primary filler content between 15% and 24% are..
Flexural Yield Strength	20.0 - 420 MPa	2900 - 60900 psi	Average value: 174 MPa Grade Count:331
Overview of materials for Nylon 66, Heat Stabilized This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Heat Stabilized". Each property range of values reported is minimum and maximum values of appr..
Flexural Yield Strength	20.0 MPa	2900 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM SILTEM-STM1500 PEI (Europe-Africa-Middle East) SILTEM STM1500 is a flexible siloxane-polyetherimide copolymer for cable and wire coatings. RoHS compliant.
Flexural Yield Strength	20.0 MPa	2900 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP 2X00858 FP-F (FEP) LNP* THERMOCOMP* 2X00858 is a compound based on FEP resin containing proprietary fillers.
Flexural Yield Strength	20.0 - 75.0 MPa	2900 - 10900 psi	Average value: 48.5 MPa Grade Count:100
Overview of materials for Polypropylene with 40% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Talc Filler". Specific grades with primary filler content between 35% and 44% are..
Flexural Yield Strength	20.0 - 150 MPa	2900 - 21800 psi	Average value: 96.3 MPa Grade Count:48
Overview of materials for Nylon 6, Cast This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Cast". Each property range of values reported is minimum and maximum values of appropriate MatW..