Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 190 MPa | 27600 psi | ISO 178, ASTM D790 |
Nilit Nilamid A G5 FR PH2 25% Glass Fiber Reinforced, Flame Retardant PA66 (with Red Phosphorous) Description: Nilamid A G5 FR PH2 combines flame retardancy with outstanding mechanical performance. This product has a complete yellow card, with RTI and CTI listings. The formulation has been optim.. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | ASTM Data |
BASF Capron® HPN 9233G 33% Glass-Filled Nylon 6 (Conditioned)
(discontinued **) Capron HPN 9233G is a 33% glass reinforced polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with excellent surface aesthetics. It is.. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | ASTM Data |
BASF Capron® SEG3 H1 15% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron SEG3 H1 is a 15% glass reinforced nylon 6 injection molding compound exhibiting. It exhibits exceptional surface aesthetics at the slower fill speeds associated with the gas assist injection .. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | ASTM D790 |
Custom Resins Vexel™ 4200 RD PBT; 30% GF, FR
(discontinued **) Property data for dry as molded samples.Data provided by the manufacturer |
|||
Flexural Yield Strength | 190 - 300 MPa | 27600 - 43500 psi | Average value: 252 MPa Grade Count:5 |
Overview of materials for Polyetherketoneetherketoneketone (PEKEKK), Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetherketoneetherketoneketone (PEKEKK), Glass Fiber Filled". Each property range of values reported i.. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | ISO 178, ASTM D790 |
Nilit Nilamid B G6 FR C4 30% Glass Fiber Reinforced, Flame Retardant PA6 Description: Nilamid B G6 FR C4 combines excellent mechanical performance with flame retardancy. The halogenated flame retardant system used in this product allows a wide range of colors. This produ.. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP DFL36EU PC LNP* Lubricomp* DFL36EU is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features include: Internally Lubricated, Easy Molding and UV Stabilized. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | ASTM D790 |
Firestone CG430-203 Nylon 6, 30% Fiberglass Filled Natural color. Heat stabilized. Fiber size is 4 mm length and 14 µm diameter.Information provided by Firestone |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | |
Idemitsu Kosan Xarec® WA 212 SPS, 30% Glass Filled Crystalline Polymer, Glass Filled, Impact Modified. Used in Automotive and Industrial applications. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | |
Idemitsu Kosan Xarec® WA 212LG SPS, 30% Glass Filled |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | ASTM D790 |
Techmer ES HiFill FR® PA4/6 GF30 FR HS X 30% Glass Filled (Dry) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Heat Stabilizer Features: Flame Retardant and Heat StabilizedUL File Number: E.. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® 4031 PBT (Europe-Africa-Middle East) VALOX 4031 is a 30% high strength glass fibre reinforced PBT injection moulding resin with excellent strength, stiffness and heat resistance. Applications: appliance handles, spotlights, electric mo.. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® 420 PBT (Europe-Africa-Middle East) VALOX 420 is a 30% glass fiber reinforced PBT injection moulding resin with excellent mechanical and thermal properties. Applications: appliance handles, spotlights, electric motors. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® 553 PBT (Europe-Africa-Middle East) VALOX 553 is a 30% glass fibre reinforced, flame retardant PBT+PC blend with good warpage characteristics. Applications: appliance handles, spotlights, electric motors, pumphousings. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® V9561 PET Flame retardant PET, 30% Glass fiber filled. Offering a good balance in CTI , GWIT , High Heat and mechanical performances. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP EFB26ER PEI (Europe-Africa-Middle East) LNP* THERMOCOMP* EFB26ER is a compound based on Polyetherimide containing Glass Fiber, Glass Bead. Added features include: Easy Molding, Mold Release. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP OF008A PPS (Asia Pacific) LNP* Thermocomp* OF008A is a compound based on PPS - Branched resin containing Glass Fiber.This product is also known as Thermocomp* OF-1008. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermocomp RF0057E PA 66 (Asia Pacific) LNP* Thermocomp* RF0057E is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant. Added features of this material include: Non-Brominated & Non-Chlorinated Flame Retardant.Thi.. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermocomp RF0057E PA 66 (Europe-Africa-Middle East) LNP* Thermocomp* RF0057E is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant. Added features of this material include: Non-Brominated & Non-Chlorinated Flame Retardant.Thi.. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Ultem LTX931A PEI Blend (Europe-Africa-Middle East) Post-industrial recycle based, 30% glass fiber filled, high flow Polyetherimide blend. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | ASTM D790 |
Techmer ES HiFill FR® PA4/6 GF30 FR HS X 30% Glass Filled (Conditioned) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Heat Stabilizer Features: Flame Retardant and Heat StabilizedUL File Number: E.. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® V8280SF PBT+PET High Modulus, PBT+PET, 40% Glass Reinforced, Mold Release, Super High Flow |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® V8280SF PBT+PET High Modulus, PBT+PET, 40% Glass Reinforced, Mold Release, Super High Flow |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | ISO 178 |
Wellman Wellamid® MRGF25/15 22H-N 25% Mineral/15% Glass Fiber Reinforced Nylon 66, Heat Stabilized Typical Applications: Lawn and garden equipment, automotive trim, bezels, wheel covers, window frames, gas tank filler housings, brackets, metalized lighting reflectors for automotive, automotive co.. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | ISO 178-93 |
Wellman Wellpet® GF100-BK1 PET, 30% Glass Fiber Reinforced Typical data obtained from injection molded test bars, tested dry as molded at 73°F (23°C). Information provided by Wellman, Inc. Engineering Resins Division. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | ASTM D790 |
E-Polymers TEKAMID® TA210GM , GF/MF Reinforced PA66, DAM GF/MF reinforced, Heat resistance, Low warpageInformation provided by E-Polymers Co. Ltd. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | ASTM D790 |
E-Polymers TEKAMID® TB120SG30 Impact Modified, 30% Glass Fiber Reinforced PA6, DAM 30% Glass Fiber reinforced, High impact resistanceInformation provided by E-Polymers Co. Ltd. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® V9561 PET (Europe-Africa-Middle East) Flame retardant PET, 30% Glass fiber filled. Offering a good balance in CTI , GWIT , High Heat and mechanical performances. |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | ASTM D790 |
Custom Resins Vexel™ 4200 RD PBT; 30% Glass Filler
(discontinued **) Property data for dry as molded samples.Data provided by the manufacturer |
|||
Flexural Yield Strength | 190 MPa | 27600 psi | ASTM D790-70 |
Budd DSM-949, Diesel Grade SMC, Vinyl Ester, Black
(discontinued **) Used for parts requiring high strength at room temperature, good retention of properties at high temperatures and corrosion resistance, such as diesel engine external body parts.Data provided by the.. |