Polymer Property : Flexural Yield Strength = 22600 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Yield Strength 156 MPa
22600 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® BFL2015 PC
Non-brominated, non-chlorinated flame retardant, glass reinforced PC. Opaque colors only
Flexural Yield Strength 156 MPa
22600 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® BFL2015 PC (Asia Pacific)
Non-brominated, non-chlorinated flame retardant, glass reinforced PC. Opaque colors only
Flexural Yield Strength 156 MPa
22600 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® BFL2015 PC (Europe-Africa-Middle East)
Non-brominated, non-chlorinated flame retardant, glass reinforced PC. Opaque colors only
Flexural Yield Strength 156 MPa
22600 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® BFL2015HF PC (Asia Pacific)
Non-brominated, non-chlorinated flame retardant, glass reinforced PC. Opaque colors only. UL94 V0 1.5 mm for BLACK; V1 1.5 mm for OTHER Color.
Flexural Yield Strength 156 MPa
22600 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® 3262R PC (Asia Pacific)
Lexan* 3262R Polycarbonate (PC) resin is a 20% glass fiber filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant GF-PC has an UL-94 V2@1.5mm rating and is available ..
Flexural Yield Strength 156 MPa
22600 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® 3412ECR PC (Europe-Africa-Middle East)
Lexan* 3412ECR Polycarbonate (PC) resin is a 20% glass fiber filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant GF-PC has an UL-94 V0 rating and is available in v..
Flexural Yield Strength 156 MPa
22600 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® 3412HF PC
20% glass reinforced, high flow PC. UL rated V-1 at 0.059"",
Flexural Yield Strength 156 MPa
22600 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP WFI18 PBT (Europe-Africa-Middle East)
LNP* Lubricomp* WFI18 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, Silicone.
Flexural Yield Strength 156 MPa
22600 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 2312EPR PEI
30% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.
Flexural Yield Strength 156 MPa
22600 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 2312EPR PEI (Asia Pacific)
30% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.
Flexural Yield Strength 156 MPa
22600 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem 2312EPR PEI (Europe-Africa-Middle East)
30% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.This data was supplied by SABIC-IP for the Eu..
Flexural Yield Strength 156 MPa
22600 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Valox® SHF434HR PBT
PBT, Super High Flow, 20% glass reinforced,hydrolytically resistant.
Flexural Yield Strength 156 MPa
22600 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Verton NV0081EV_GY7E149 PC+ABS
Preliminary data for 40% long fiber single pellet non-halogen FR color filled PC/ABSThis data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength 156 MPa
22600 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® 3412ECR PC
Lexan* 3412ECR Polycarbonate (PC) resin is a 20% glass fiber filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant GF-PC has an UL-94 V0 rating and is available in v..
Flexural Yield Strength 156 MPa
22600 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® 3412ECR PC (Asia Pacific)
Lexan* 3412ECR Polycarbonate (PC) resin is a 20% glass fiber filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant GF-PC has an UL-94 V0 rating and is available in v..
Flexural Yield Strength 156 MPa
22600 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® 3412HF PC (Asia Pacific)
20% glass reinforced, high flow PC. UL rated V-1 at 0.059"",