Polymer Property : Flexural Yield Strength = 225 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Yield Strength 225 MPa
32600 psi
ISO 178
Wellman Wellamid® GFT33N051-N2 33% Impact Modified Glass Reinforced Nylon 66/6, Lubricated & Heat Stabilized &n
Typical Applications: Machinery gear trains and linkage, conveyor belt links, fasteners, auto under hood and door parts, automotive door handles, appliance parts, sporting goods, lawn and garden equ..
Flexural Yield Strength 225 MPa
32600 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 2200F PEI
20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors.
Flexural Yield Strength 225 MPa
32600 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 2300F PEI
30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors.
Flexural Yield Strength 225 MPa
32600 psi
2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM 2300F PEI
30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors.
Flexural Yield Strength 225 MPa
32600 psi
2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM 2310F PEI
30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors.
Flexural Yield Strength 225 MPa
32600 psi
2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM AR9300 PEI (Europe-Africa-Middle East)
30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution.
Flexural Yield Strength 225 MPa
32600 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Ultem ATX203R PEI+PCE
30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength 225 MPa
32600 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Ultem ATX203R PEI+PCE (Asia Pacific)
30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Yield Strength 225 MPa
32600 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Ultem ATX203R PEI+PCE (Europe-Africa-Middle East)
30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Europe-Africa-Middle East regio..
Flexural Yield Strength 225 MPa
32600 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ULTEM HU2110 PEI
10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP ..
Flexural Yield Strength 225 MPa
32600 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ULTEM HU2200 PEI
20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP ..
Flexural Yield Strength 225 MPa
32600 psi
2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM HU2300 PEI
30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP ..
Flexural Yield Strength 225 MPa
32600 psi
2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM HU2310 PEI
30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP..
Flexural Yield Strength 225 MPa
32600 psi
2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM HU2310 PEI (Asia Pacific)
30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP..
Flexural Yield Strength 225 MPa
32600 psi
2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM HU2310 PEI (Europe-Africa-Middle East)
30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). RoHS compliant. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP..
Flexural Yield Strength 225 MPa
32600 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Valox® V9290 PET (Europe-Africa-Middle East)
45% GF PET, Glass, Mold Release, Heat Stabilized,
Flexural Yield Strength 225 MPa
32600 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP Thermocomp PF0069 PA 6 (Europe-Africa-Middle East)
LNP* STARFLAM* PF0069 is a compound based on PA 6 resin containing Glass Fiber, Flame Retardant. Added features include; Flame Retardant.This data was supplied by SABIC-IP for the Europe-Africa-Midd..
Flexural Yield Strength 225 MPa
32600 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL GFN1740V PPE+PS
Noryl* GFN1740V Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 40 % Glass Reinforced, injection moldable grade with improved hydrolytic stability and with a Tensile Modulus > 11000 MPa; thi..
Flexural Yield Strength 225 MPa
32600 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL GFN1740V PPE+PS (Asia Pacific)
Noryl* GFN1740V Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 40 % Glass Reinforced, injection moldable grade with improved hydrolytic stability and with a Tensile Modulus > 11000 MPa; thi..
Flexural Yield Strength 225 MPa
32600 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL GFN1740V PPE+PS (Europe-Africa-Middle East)
Noryl* GFN1740V Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 40 % Glass Reinforced, injection moldable grade with improved hydrolytic stability and with a Tensile Modulus > 11000 MPa; thi..
Flexural Yield Strength 225 MPa
32600 psi
ASTM D790
Tipco Tipcofil® AG 800 - 40% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability
40% Glass Reinforced Nylon-6 CompoundApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd., India.
Flexural Yield Strength 225 MPa
32600 psi
2 mm/min; ISO 178
Eurostar Starflam PF0069 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded
Starflam PF0069 is a Flame Retardant, Glass Fiber Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.