Polymer Property : Flexural Yield Strength = 21500 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Yield Strength 148 - 262 MPa
21500 - 38000 psi
Average value: 219 MPa Grade Count:16
Overview of materials for Polyphenylene Sulfide (PPS) with Carbon Fiber + PTFE Filler
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with Carbon Fiber + PTFE Filler". Each property range of values reported is ..
Flexural Yield Strength 148 MPa
21500 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem 2412EPR PEI
40% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.This data was supplied by SABIC-IP for the Am..
Flexural Yield Strength 148 MPa
21500 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem 2412EPR PEI (Asia Pacific)
40% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.This data was supplied by SABIC-IP for the As..
Flexural Yield Strength 148 MPa
21500 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem 2412EPR PEI (Europe-Africa-Middle East)
40% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.This data was supplied by SABIC-IP for the Eu..
Flexural Yield Strength 148 MPa
21500 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Valox® 855 PBT (Europe-Africa-Middle East)
VALOX 855 is 15% glass reinforced PBT+PET blend with improved surface appearance. Applications: external housings, steam irons, appliance housings and lighting parts.
Flexural Yield Strength 148 MPa
21500 psi
ASTM D790
Star Plastics PC1212FR Molding Grade PC FR
Information provided by Star Plastics, Inc.
Flexural Yield Strength 148 MPa
21500 psi
ASTM D790
Star Plastics PC1212FRR Molding Grade PC FR
Information provided by Star Plastics, Inc.
Flexural Yield Strength 148 MPa
21500 psi
ASTM D790
Star Plastics PC1212FRRUV Molding Grade PC FR
Information provided by Star Plastics, Inc.
Flexural Yield Strength 148 MPa
21500 psi
ASTM D790
Star Plastics PC1212FRUV Molding Grade PC FR
Information provided by Star Plastics, Inc.
Flexural Yield Strength 148 MPa
21500 psi
ASTM D790
Star Plastics PCGF30 Molding Grade PC with 30% Glass
Information provided by Star Plastics, Inc.
Flexural Yield Strength 148 MPa
21500 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP EX00781H PEI
LNP* THERMOCOMP* EX00781H is a compoud based on Polyetherimide containng Proprietary Filler(s). Added feature of this material is: Healthcare.
Flexural Yield Strength 148 MPa
21500 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP SF00A PA12
LNP* THERMOCOMP* SF00A is a compound based on Nylon 12 resin containing 50% Glass Fiber.
Flexural Yield Strength 148 MPa
21500 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Thermocomp SF00A PA12 (Europe-Africa-Middle East)
Glass filled Nylon 12This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Yield Strength 148 MPa
21500 psi
2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics NORYL PX4605 PPE+PS
PPE+PS blend. 20% Glass reinforced. High heat. Dimensional stability. Suitable for automotive and E/E applications.
Flexural Yield Strength 148 MPa
21500 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP SF00A PA12 (Asia Pacific)
Glass filled Nylon 12
Flexural Yield Strength 148 MPa

@Temperature 23.0 °C
21500 psi

@Temperature 73.4 °F
Hexcel® HexPly® 954-6 Curing Cyanate Resin
HexPly® 954-6 is a 250°F (121°C) curing toughened cyanate resin with 300°F (149°C) Tg. HexPly® 954-6 is formulated for autoclave curing. Recommended cure is three hours at 250°F (121°C). Ser..
Flexural Yield Strength 148 MPa
21500 psi
ASTM D790
Tipco Tipcofil® AGM 802 - 25% Mineral & 15% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability
25% Mineral + 15% Glass Reinforced Nylon-6 CompoundApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd., India.