Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 20.0 MPa | 2900 psi | ASTM D790 |
Multibase Multi-Pro® 3011 CHI Polypropylene Calcium Carbonate Filler, 30% by weight.Forms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase |
|||
Flexural Yield Strength | 20.0 MPa | 2900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
Ovation Polymers Opnyl OP6MT254 Nylon 6 Nylon 6 – Mighty Tough plasticized extrusion grade for tubing/profile applications. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are p.. |
|||
Flexural Yield Strength | 20.0 MPa | 2900 psi | ASTM D580 |
Protective Coating PC-7® Epoxy Paste PC-7® is a tough job Epoxy formulation developed for maximum bonding power. Components A (grey) and B (black), when mixed, react to form a bond of good strength. PC-7® formulation provides exten.. |
|||
Flexural Yield Strength | 20.0 MPa | 2900 psi | ASTM D580 |
Protective Coating PC-SuperEpoxy™ Translucent Epoxy Putty PC-SUPEREPOXY™ is a non-drip, thixotropic, translucent paste with unlimited uses in bonding, sealing, and as a filler for most materials. Unlike conventional liquid epoxies, PC-SUPEREPOXY™ can be.. |
|||
Flexural Yield Strength | 20.0 - 180 MPa | 2900 - 26100 psi | Average value: 44.5 MPa Grade Count:58 |
Overview of materials for Polypropylene, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Molded". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Flexural Yield Strength | 20.0 - 88.0 MPa | 2900 - 12800 psi | Average value: 46.6 MPa Grade Count:74 |
Overview of materials for Polypropylene with 30% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Talc Filler". Specific grades with primary filler content between 25% and 34% are.. |
|||
Flexural Yield Strength | 20.0 - 51.0 MPa | 2900 - 7400 psi | Average value: 32.2 MPa Grade Count:28 |
Overview of materials for Polypropylene with 20% Mica Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Mica Filler". Specific grades with primary filler content between 15% and 24% are.. |
|||
Flexural Yield Strength | 20.0 - 420 MPa | 2900 - 60900 psi | Average value: 174 MPa Grade Count:331 |
Overview of materials for Nylon 66, Heat Stabilized This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Heat Stabilized". Each property range of values reported is minimum and maximum values of appr.. |
|||
Flexural Yield Strength | 20.0 MPa | 2900 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics ULTEM SILTEM-STM1500 PEI (Europe-Africa-Middle East) SILTEM STM1500 is a flexible siloxane-polyetherimide copolymer for cable and wire coatings. RoHS compliant. |
|||
Flexural Yield Strength | 20.0 MPa | 2900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP 2X00858 FP-F (FEP) LNP* THERMOCOMP* 2X00858 is a compound based on FEP resin containing proprietary fillers. |
|||
Flexural Yield Strength | 20.0 - 75.0 MPa | 2900 - 10900 psi | Average value: 48.5 MPa Grade Count:100 |
Overview of materials for Polypropylene with 40% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Talc Filler". Specific grades with primary filler content between 35% and 44% are.. |
|||
Flexural Yield Strength | 20.0 - 150 MPa | 2900 - 21800 psi | Average value: 96.3 MPa Grade Count:48 |
Overview of materials for Nylon 6, Cast This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Cast". Each property range of values reported is minimum and maximum values of appropriate MatW.. |