- Polymer Property : Flexural Yield Strength = 196 MPa
Polymer Property : Flexural Yield Strength = 196 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Yield Strength | 196 MPa | 28400 psi | 23°C; 50% RH; ASTM D570 |
| PTS Lucet® GC-225 25% Glass Reinforced Acetal Copolymer Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
| Flexural Yield Strength | 196 MPa | 28400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL38 PC LNP* Lubricomp* DFL-4038 is a Polycarbonate containing 40% Glass Fiber, 15% PTFE. Added features include: Internally Lubricated. |
|||
| Flexural Yield Strength | 196 MPa @Thickness 3.20 mm |
28400 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| LG Chemical LUCEL GC225 POM+GF25%, High Rigidity Feature: Injection Molding, POM+GF25%, High RigidityApplication: Casings of Pump and Pivot BearingsCAS No. 66455-31-0 and 65997-17-3Information provided by LG Chemical |
|||
| Flexural Yield Strength | 196 MPa @Thickness 3.20 mm |
28400 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| LG Chemical LUMID LW4403A(W) PA66+GF/MF40%, Low Warpage Feature: Injection Molding, PA66+GF/MF40%, Low WarpageApplication: Automotive (Timing Belt Cover)CAS No. 25038-54-4, 13983-17-0 and 65997-17-3Information provided by LG Chemical |
|||
| Flexural Yield Strength | 196 MPa | 28400 psi | DIN 53455; ASTM D790 |
| Kolon KOPA® KN333G15 G/F Reinforced Nylon 66 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstandin.. |
|||
| Flexural Yield Strength | 196 MPa | 28400 psi | DIN 53455; ASTM D790 |
| Kolon KOPA® KN135HB30HI Multi Reinforced Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
| Flexural Yield Strength | 196 MPa | 28400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Valox® IQ507 PBT+PC Valox iQ507 resin: Environmentally responsible, sustainable, and low carbon footprint resin that is 30% glass fiber reinforced PBT+PC alloy. Valox iQ507 offers good mechanical and thermal characte.. |
|||
| Flexural Yield Strength | 196 MPa | 28400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Valox® IQ507 PBT+PC (Asia Pacific) Valox iQ507 resin: Environmentally responsible, sustainable, and low carbon footprint resin that is 30% glass fiber reinforced PBT+PC alloy. Valox iQ507 offers good mechanical and thermal characte.. |
|||
| Flexural Yield Strength | 196 MPa | 28400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Valox® IQ507 PBT+PC (Europe-Africa-Middle East) Valox iQ507 resin: Environmentally responsible, sustainable, and low carbon footprint resin that is 30% glass fiber reinforced PBT+PC alloy. Valox iQ507 offers good mechanical and thermal characte.. |
|||
| Flexural Yield Strength | 196 MPa | 28400 psi | ASTM D790 |
| Shinkong Synthetic Fibers Shinite® T101G30 PET, 30% Glass Filled Information from Shinkong Synthetic Fibers Corp. |
|||
| Flexural Yield Strength | 196 MPa | 28400 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP LF004E PEEK (Europe-Africa-Middle East) LNP* THERMOCOMP* LF004E is a compound based on Polyetheretherketone resin containing Glass Fiber. Added features include: Easy Molding. |
|||
| Flexural Yield Strength | 196 MPa | 28400 psi | ASTM D790 |
| Samyang Tribit® 1500G30 Polybutylene Terephthalate, 30% Glass Reinforced Characteristics:G/F reinforcedHeat and Impact resistantApplications:AutomotiveConnectorGearOutdoor handleIgnition systemElectronicConnectorGas valveCoil bobbinSwitch caseRelay caseO/A partsAll infor.. |
|||
| Flexural Yield Strength | 196 MPa | 28400 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP QF0069 PA6.10 (Europe-Africa-Middle East) LNP* THERMOCOMP* QF0069 is a compound based on PA610 resin contaning Glass Fiber, Flame Retardant. Added features include: Flame retardant. |
|||
| Flexural Yield Strength | 196 MPa | 28400 psi | ASTM D790 |
| Shinkong Synthetic Fibers Shinite® T101G30 PET, 30% Glass Filled Information from Shinkong Synthetic Fibers Corp. |
|||
| Flexural Yield Strength | 196 MPa | 28400 psi | ASTM D790 |
| Shinkong Synthetic Fibers Shinite® E202G30 PBT, 30% Glass Filled Information from Shinkong Synthetic Fibers Corp. |
|||
| Flexural Yield Strength | 196 MPa | 28400 psi | ASTM D790 |
| Shinkong Synthetic Fibers Shinite® E202G30 PBT, 30% Glass Filled Information from Shinkong Synthetic Fibers Corp. |
|||
| Flexural Yield Strength | 196 MPa | 28400 psi | ASTM D790 |
| Toyobo Vylopet® EMC120S Glass Reinforced Polyester, Standard Grade Key Feature: Flame retardant V-0 UL-94 classApplications: Electric and electronic componentsGeneral features of Vylopet® include heat resistance, good mechanical properties, high dielectric strengt.. |
|||
| Flexural Yield Strength | 196 MPa | 28400 psi | ASTM D790 |
| Cheng Yu Plastic A707G25 SAN, 25% Glass Fiber |
|||
| Flexural Yield Strength | 196 MPa | 28400 psi | DIN 53455; ASTM D790 |
| Kolon KOPA® KN3321G15VO G/F Reinforced & Flame Retardant Nylon 66 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstanding .. |
|||
| Flexural Yield Strength | 196 MPa @Thickness 3.20 mm |
28400 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| LG Chemical LUMID LW4009A(W) PA6+GF/MF40%, Low Warpage Feature: Injection Molding, PA6+GF/MF40%, Low WarpageApplication: Automotive (Timing Belt Cover)CAS No. 25038-54-4, 13983-17-0 and 65997-17-3Information provided by LG Chemical |
|||