Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 193 MPa | 28000 psi | ASTM D790 |
PolyOne Stat-Tech™ PI-05CF/000 Polyetherimide - 5% Carbon Fibers - ESD Applications
(discontinued **) Data provided by PolyOne. |
|||
Flexural Yield Strength | 193 - 330 MPa | 28000 - 47900 psi | Average value: 263 MPa Grade Count:26 |
Overview of materials for Nylon 66, 20% Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 20% Carbon Fiber Filled". Specific grades with carbon fiber content between 15% and 24% are in.. |
|||
Flexural Yield Strength | 193 MPa | 28000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP IFL36L PA6.12 LNP* LUBRICOMP* IFL36L is a compound based on Nylon 6/12 containing 30% Glass Fiber, 15% PTFE. Added features of this grade include: Low Extractable, Wear Resistant. |
|||
Flexural Yield Strength | 193 MPa | 28000 psi | ASTM D790 |
Techmer ES Electrafil® J-50/CF/30/TF/13/SI/2 Polycarbonate, 30% Carbon Fiber Reinforced, 13% PTFE, 2% Silicone |
|||
Flexural Yield Strength | 193 MPa | 28000 psi | ASTM D790 |
Techmer ES Plastiblend® PBT/ABS GF30 BK 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAppearance: BlackInformation provided by TP Composites, Inc. |
|||
Flexural Yield Strength | 193 MPa | 28000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermocomp WC003 PBT (Europe-Africa-Middle East) LNP* Thermocomp* WC003 is a compound based on Polybutylene Terephalate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABI.. |
|||
Flexural Yield Strength | 193 MPa | 28000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP WC003 PBT (Europe-Africa-Middle East) LNP* Thermocomp* WC003 is a compound based on Polybutylene Terephalate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Flexural Yield Strength | 193 MPa | 28000 psi | ASTM D790 |
Techmer ES HiFill FR® PET GF30 FR X 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightFeatures: Flame RetardantInformation provided by TP Composites, Inc. |
|||
Flexural Yield Strength | 193 MPa | 28000 psi | Flexural elongation is 1%; ASTM D790 |
Toyobo TS101 PPS, Glass Fiber/Mineral Reinforced Key Feature: High dimensional stabilityHigh performance injection-molding resin created from crystalline polyphenylene sulfide, using a special formulation technology developed by Toyobo. Excellent.. |
|||
Flexural Yield Strength | 193 MPa | 28000 psi | ASTM D790 |
Clariant Renol 66G33 2% Moly Nylon 66, 33% Glass Fiber Reinforced, 2% Molybdenum Disulfide Lubricated Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 193 MPa | 28000 psi | ASTM D790 |
Clariant Renol 66G33HSL Nylon 66, 33% Glass Fiber Reinforced, Heat Stabilized, Lubricated Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 193 MPa | 28000 psi | ASTM D790 |
Chem Polymer Chemlon 125 G Nylon 66, 25% Glass Sphere Reinforced A 25% glass sphere reinforced nylon 66 offering a balance of rigidity, dimensional stability and surface appearance.Data provided by the manufacturer, Chem Polymer. |
|||
Flexural Yield Strength | 193 MPa | 28000 psi | ASTM D790 |
Chem Polymer Chemlon 225-15 MG Nylon 6, 25% Mineral/15% Glass Fiber Reinforced A 25% mineral reinforced, 15% glass fiber reinforced nylon 6 offering excellent rigidity, dimensional stability and warpage control in large area parts.Data provided by the manufacturer, Chem Polyme.. |
|||
Flexural Yield Strength | 193 MPa | 28000 psi | ASTM D790 |
Clariant Renol 66G33-L Nylon 66, 33% Glass Fiber Reinforced, Lubricated Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 193 MPa | 28000 psi | ASTM D790 |
Performance Polymers IPS II PPL-C1050 PEKK (Polyetherketoneketone) Linear Extrusion Grade Amber pellets; neat resinInformation provided by Infinite Polymer System II. |
|||
Flexural Yield Strength | 193 MPa | 28000 psi | ASTM D790 |
Performance Polymers IPS II PPL-C4050 PEKK (Polyetherketoneketone) Linear Molding Grade Amber pellets; neat resinInformation provided by Infinite Polymer System II. |
|||
Flexural Yield Strength | 193 MPa | 28000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM AR9100 PEI 10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming. |