Polymer Property : Flexural Yield Strength = 19100 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	132 MPa	19100 psi	1.3 mm/min; ASTM D790
Ovation Polymers RIGITRON 10020 GF Polycarbonate, 20% Glass Reinforced PC - Glass reinforced (20 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared accor..
Flexural Yield Strength	132 MPa	19100 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Lubricomp DFP22H PC LNP* Lubricomp* DFP22H is a compound based on Polycarbonate containing Glass Fiber and PTFE. Characteristics of this grade are: Internally Lubricated and Healthcare.This data was supplied by SABIC..
Flexural Yield Strength	132 MPa	19100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP DFL12 PC LNP* Lubricomp* DFL12 is a compound based on Polycarbonate resin containing 10% Glass Fiber and 5% PTFE. Added features include: Internally Lubricated.
Flexural Yield Strength	132 MPa	19100 psi	50 mm/min; ASTM D790
LG Chemical 95HC SAN Resin Heat and chemical resistance, Good mechanical properties, Excellent processability, Superior transparency, Good dimensional stability, Applications include make-up cases and other products requiring..
Flexural Yield Strength	132 MPa	19100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-LOY ZF3021 PPE+PS (Europe-Africa-Middle East) LNP* STAT-LOY* ZF3021 is a compound based on PPE + PS Blend resin containing Glass Fiber. Added features include Antistatic, Flame Retardant.
Flexural Yield Strength	132 MPa	19100 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Thermocomp DFZ22E PC LNP* Thermocomp* DFZ22E is a compound based on Polycarbonate with Glass and Milled Fiber. Characteristics of this products is Easy Molding.This data was supplied by SABIC-IP for the Americas region..
Flexural Yield Strength	132 MPa	19100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP WFB33E PBT (Europe-Africa-Middle East) LNP THERMOCOMP WFB33E is a compound based on Polybutylene Terephalate resin containing Glass Fiber and Glass Bead. Added features include Easy Molding.
Flexural Yield Strength	132 MPa	19100 psi	Neat Resin; ASTM D790
Hexcel® HexFlow® RTM 6 180°C Epoxy System for Resin Transfer Molding Monocomponent System HexFlow® RTM 6 is a monocomponent resin already degassed, specifically developed to fulfill the requirements of the aerospace and space industries in advanced resin transfer moulding (RTM) process...
Flexural Yield Strength	132 - 269 MPa	19100 - 39000 psi	Average value: 209 MPa Grade Count:8
Overview of materials for Polyethylene Terephthalate (PET), 40% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 40% Glass Reinforced". Specific grades with glass content between 35% ..
Flexural Yield Strength	132 MPa	19100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP GFL36 PSU (Europe-Africa-Middle East) LNP* Lubricomp* GFL36 is a compound based on Polysulfone resin containing Glass Fiber, PTFE. Added features include: Internally Lubricated.