Polymer Property : Flexural Yield Strength = 188 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Yield Strength 188 MPa

@Thickness 3.20 mm
27300 psi

@Thickness 0.126 in
1.3mm/min; ASTM D790
LG Chemical Lupox® GP2306FG PBT+GF30%
Description: Injection Molding, PBT+GF30%, Flame Retardant Application: IT/OA, E&E (Connector)CAS No. 71342-77-3, 65997-17-3, 24968-12-5, 25038-59-9 and 1309-64-4Information provided by LG Chemical
Flexural Yield Strength 188 MPa
27300 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP UX05051 PPA (Europe-Africa-Middle East)
Internally lubricated Polyphthalamide compound, containing Glass Fiber and PTFE. Added features include Heat Stabilized, Flame Retardant and Hot Water Moldable
Flexural Yield Strength 188 MPa
27300 psi
ASTM D790
Techmer ES HiFill® PPS GF/M65 BK 65% Glass/Mineral Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass/Mineral, 65% Filler by WeightAppearance: BlackInformation provided by TP Composites, Inc.
Flexural Yield Strength 188 MPa
27300 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP DF004XXC PC (Europe-Africa-Middle East)
Polycarbonate compound, countaining Glass Fiber
Flexural Yield Strength 188 MPa
27300 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Valox® IQNH4565 PBT (Asia Pacific)
Valox* iQNH4565 resin is a non-brominated/non-chlorinated flame retardant product based on an environmentally sustainable Valox iQ* PBT resin. Post-consumer recycle (PCR) usage is 29% based on EPEAT..
Flexural Yield Strength 188 MPa
27300 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Valox® IQNH4565 PBT (Asia Pacific)
Valox* iQNH4565 resin is a non-brominated/non-chlorinated flame retardant product based on an environmentally sustainable Valox iQ* PBT resin. Post-consumer recycle (PCR) usage is 29% based on EPEAT..