Polymer Property : Flexural Yield Strength = 182 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	182 MPa	26400 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® HFD4413 PC Lexan* HFD4413 is a 30% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release.
Flexural Yield Strength	182 MPa	26400 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® HFD4413 PC (Asia Pacific) Lexan* HFD4413 is a 30% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release.
Flexural Yield Strength	182 MPa	26400 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-KON DE0026E PC (Europe-Africa-Middle East) LNP* Stat-kon* DE0026E is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant.
Flexural Yield Strength	182 MPa	26400 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-KON RX06001 PA 66 (Europe-Africa-Middle East) LNP* Stat-kon* RX06001 is a compound based on Nylon 66 resin containing Carbon Fiber. Added features of this material include: Easy Molding, High Impact, Electrically Conductive.
Flexural Yield Strength	182 MPa	26400 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP DX10311 PC (Asia Pacific) DX10311 is 30% glass fiber reinforced, impact modified polycarbonate resin. High flow and good ductility.
Flexural Yield Strength	182 MPa	26400 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem ATX102R PEI+PCE 20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength	182 MPa	26400 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem ATX102R PEI+PCE (Asia Pacific) 20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Yield Strength	182 MPa	26400 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem ATX102R PEI+PCE (Europe-Africa-Middle East) 20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region..
Flexural Yield Strength	182 MPa	26400 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® HFD4413 PC (Europe-Africa-Middle East) Lexan* HFD4413 is a 30% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release.