Polymer Property : Flexural Yield Strength = 17500 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	121 - 255 MPa	17500 - 37000 psi	Average value: 181 MPa Grade Count:55
Overview of materials for Polycarbonate, Carbon + PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Carbon + PTFE Filled". Each property range of values reported is minimum and maximum valu..
Flexural Yield Strength	121 - 355 MPa	17500 - 51500 psi	Average value: 222 MPa Grade Count:62
Overview of materials for Nylon 610, Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 610, Glass Reinforced". Each property range of values reported is minimum and maximum values of ap..
Flexural Yield Strength	121 MPa	17500 psi	ASTM D790
Star Plastics PCGF20 Molding Grade PC with 20% Glass Information provided by Star Plastics, Inc.
Flexural Yield Strength	121 MPa	17500 psi	ASTM D790
Techmer ES HiFillÂ® PP E GF40 CC 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by WeightAdditive: Heat StabilizerFeatures: Chemically Coupled, Heat Stabilized and High Viscosit..
Flexural Yield Strength	121 MPa	17500 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL NH6020 PPE+HIPS Noryl NH6020 resin is an unfilled, injection moldable modified polyphenylene ether resin. Designed for high heat resistance and thin wall FR performance, this resin delivers a UL94 V0 rating at 0.8 ..
Flexural Yield Strength	121 MPa	17500 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL NH6020 PPE+HIPS (Asia Pacific) Noryl NH6020 resin is an unfilled, injection moldable modified polyphenylene ether resin. Designed for high heat resistance and thin wall FR performance, this resin delivers a UL94 V0 rating at 0.8 ..
Flexural Yield Strength	121 MPa	17500 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL NH6020 PPE+HIPS (Europe-Africa-Middle East) Noryl* NH6020 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for high heat resistance and thin wall FR performance, this resin delivers a UL94 V0 rating at 0.8 mm an..
Flexural Yield Strength	121 MPa	17500 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-LOY PF303 PA 6 LNP* STAT-LOY* PF303 is a Nylon 6 base resin containing 15% Glass Fiber. Added features of this grade includes: Antistat.
Flexural Yield Strength	121 MPa	17500 psi	6.4 mm; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP Noryl_FM4025 PPE+HIPS (Europe-Africa-Middle East) LNP* Thermocomp* Noryl_FM4025 compound is GR/MR 40%, high modulus structural foam. 10% weight reduction, 0.250"" wall thickness.
Flexural Yield Strength	121 MPa	17500 psi	6.4 mm; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP Noryl_FM4025 PPE+PS LNP* Thermocomp* Noryl_FM4025 compound is GR/MR 40%, high modulus structural foam. 10% weight reduction, 0.250"" wall thickness.
Flexural Yield Strength	121 MPa	17500 psi	ASTM D790
Chem Polymer Chemlon 100 W Nylon 66, MoS2 Filled A molybdenum disulfide modified nylon 66 exhibiting superior tensile strength and wear resistance, greater dimensional stability and higher heat resistance than general purpose nylon 66.Data provide..
Flexural Yield Strength	121 - 210 MPa	17500 - 30500 psi	Average value: 161 MPa Grade Count:18
Overview of materials for Polyethersulfone (PES), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 10% Glass Fiber Filled". Specific grades with glass content between 5% and 14% a..