Polymer Property : Flexural Yield Strength = 175 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Yield Strength 175 MPa
25400 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics EXTEM UH1006 TPI Blend
High Heat Amorphous TPI Blend, Excellent Chemical Resistance, High Continuous Use Temperature (CUT), Best-in-class FR, OSU and LOI. Material is UL-listed. This material is RoHS compliant and also ha..
Flexural Yield Strength 175 MPa
25400 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics EXTEM UH1006 TPI Blend (Asia Pacific)
High heat amorphous TPI Blend, Chemical Resistant
Flexural Yield Strength 175 MPa
25400 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics EXTEM UH1006 TPI Blend (Europe-Africa-Middle East)
High heat amorphous TPI Blend, Chemical Resistant
Flexural Yield Strength 175 MPa
25400 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics EXTEM UH1006M TPI Blend
High heat amorphous TPI Blend, Chemical Resistant
Flexural Yield Strength 175 MPa
25400 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics EXTEM UH1006M TPI Blend (Asia Pacific)
High heat amorphous TPI Blend, Chemical Resistant
Flexural Yield Strength 175 MPa
25400 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics EXTEM UH1006M TPI Blend (Europe-Africa-Middle East)
High heat amorphous TPI Blend, Chemical Resistant
Flexural Yield Strength 175 MPa
25400 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics EXTEM UH1016 TPI Blend (Europe-Africa-Middle East)
High heat amorphous TPI Blend, Chemical Resistant, High Flow
Flexural Yield Strength 175 MPa
25400 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Extem UH1016M TPI Blend (Asia Pacific)
High heat amorphous TPI Blend, Chemical ResistantThis data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Yield Strength 175 MPa
25400 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Extem UH1016M TPI Blend (Europe-Africa-Middle East)
High heat amorphous TPI Blend, Chemical ResistantThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Yield Strength 175 MPa
25400 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics EXTEM UH1026 TPI Blend
High heat amorphous TPI Blend, Chemical Resistant, High Flow, IR-Transparent
Flexural Yield Strength 175 - 840 MPa
25400 - 122000 psi
Average value: 310 MPa Grade Count:127
Overview of materials for Nylon 6, 50% Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. E..
Flexural Yield Strength 175 - 455.054 MPa

@Temperature -40.0 - 149 °C
25400 - 66000.1 psi

@Temperature -40.0 - 300 °F
Average value: 264 MPa Grade Count:6
Overview of materials for Nylon 66, 50% Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. ..
Flexural Yield Strength 175 MPa
25400 psi
ISO 178
Solvay Technyl® A 218 V30 Nylon 66, 30% Glass Fiber, EH50
Polyamide PA66, reinforced with 30% of glass fiber, heat stabilized, for injection molding.Technyl A 218 V30 is used in all sectors of industry, offering an excellent combination between thermal and..
Flexural Yield Strength 175 MPa
25400 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Valox® 5031 PBT (Europe-Africa-Middle East)
VALOX 5031 is a 30% glass reinforced PBT+PC blend with low warpage characteristics. Applications: appliance handles, automotive doorhandles. This grade is a 508 with reduced warpage.
Flexural Yield Strength 175 MPa
25400 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Valox® ENH4550 PBT (Europe-Africa-Middle East)
25% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin.
Flexural Yield Strength 175 MPa
25400 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Valox® ENH4560 PBT (Asia Pacific)
Valox* ENH4560 resin is a non-brominated/non-chlorinated flame retardant product based on Valox* iQ PBT resin.
Flexural Yield Strength 175 MPa
25400 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Valox® IQNH4560 PBT (Asia Pacific)
Valox* IQNH4560 resin is a non-brominated/non-chlorinated flame retardant product based on Valox* iQ PBT resin.
Flexural Yield Strength 175 MPa
25400 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP DX06313I PC (Asia Pacific)
DX06313I is 30% glass fiber reinforced, impact modified polycarbonate resin. High flow and good ductility.
Flexural Yield Strength 175 MPa
25400 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP OF006 PPS - Linear
LNP* THERMOCOMP* OF006 is a compound based on Linear PPS containing 30% Glass Fiber.
Flexural Yield Strength 175 MPa
25400 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP VERTON MV008 PP (Europe-Africa-Middle East)
LNP* VERTON* MV008 is a compound based on Polypropylene resin containing Long Glass. Added features include Chemically Coupled.
Flexural Yield Strength 175 MPa
25400 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL GFN1630V PPE+HIPS
Noryl* GFN1630V Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 30 % Glass Reinforced, injection moldable grade with improved hydrolytic stability; this grade has been developed for fluid en..
Flexural Yield Strength 175 MPa
25400 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL GFN1630V PPE+HIPS (Asia Pacific)
Noryl* GFN1630V Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 30 % Glass Reinforced, injection moldable grade with improved hydrolytic stability; this grade has been developed for fluid en..
Flexural Yield Strength 175 MPa
25400 psi
2 mm/min; ISO 178
SABIC Innovative Plastics NORYL GTX GTX8120P PPE+PA (Europe-Africa-Middle East)
GTX8120P is a glass filled extrudable Noryl GTX with low thermal conductivity, suitable for thermal breaks
Flexural Yield Strength 175 MPa
25400 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-KON DE003M PC
LNP* STAT-KON* DE003M is a compound based on Polycarbonate containing 15% Milled Carbon Fiber. Added feature of this grade is: Electrically Conductive.
Flexural Yield Strength 175 MPa
25400 psi
ASTM D790
Tipco Tipcofil® AG 300 - 15% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability
15% Glass Reinforced Nylon-6 CompoundApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd., India.
Flexural Yield Strength 175 MPa
25400 psi
ISO 178
Wellman Wellamid® GF13-66 22LH-N 13% Glass Fiber Reinforced Nylon 66, Lubricated & Heat Stabilized
Typical Applications: Radio and TV components, dishwasher roller carriages, chain saw oil reservoirs, gears, housings, door & window latches, power hand tool housings, high temperature devices.Data ..
Flexural Yield Strength 175 MPa
25400 psi
ISO 178
Wellman Wellamid® GF13-66 XE-N 13% Glass Fiber Reinforced Nylon 66, Lubricated & Heat Stabilized
Typical Applications: Radio and TV components, dishwasher roller carriages, chain saw oil reservoirs, gears, housings, door & window latches, power hand tool housings, high temperature devices.Data ..
Flexural Yield Strength 175 MPa
25400 psi
ASTM Data
BASF Capron® HPN 9315G Impact Modified, 15% Glass-Filled Nylon 6 (Dry)  (discontinued **)
Capron HPN 9315G is a 15% glass reinforced, impact modified polyamide 6 injection molding grade resin in the High Productivity Nylon Series developed for applications requiring superior dry-as-molde..
Flexural Yield Strength 175 MPa
25400 psi
ASTM D790
Solvay Specialty Polymers Ixef® 2530/X9027 Polyarylamide, 55% Mineral + Glass Fiber, at Equilibrium (65% RH)  
The IXEF compounds are a family of semi-crystalline polyarylamide thermoplastics reinforced with glass fibers and/or mineral fillers for injection molding.Data provided by the manufacturer, Solvay A..
Flexural Yield Strength 175 MPa
25400 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Valox® VX4930 PBT (Europe-Africa-Middle East)
VALOX VX4930 is a 30% glass reinforced nucleated PBT/ASA blend with excellent mechanical properties, high dimensional stability and low density. Applications: connectors and automotive industry.