- Polymer Property : Flexural Yield Strength = 17100 psi
Polymer Property : Flexural Yield Strength = 17100 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Yield Strength | 118 MPa | 17100 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL22 PC (Asia Pacific) LNP* Lubricomp* DFL22 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
| Flexural Yield Strength | 118 MPa | 17100 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL32 PC (Europe-Africa-Middle East) LNP* Lubricomp* DFL32 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. |
|||
| Flexural Yield Strength | 118 MPa | 17100 psi | ASTM D790 |
| Kolon Kocetal® CL704 Reinforced Grade Acetal Copolymer
(discontinued **) Thermal properties: Kocetal has excellent heat stability; heat degradation is little under long term and high temperature application, compared to other POM. Maximum applicable temperature of produ.. |
|||
| Flexural Yield Strength | 118 MPa | 17100 psi | ASTM D790 |
| Kolon Kocetal® WH702 Reinforced Grade Acetal Copolymer
(discontinued **) Thermal properties: Kocetal has excellent heat stability; heat degradation is little under long term and high temperature application, compared to other POM. Maximum applicable temperature of produ.. |
|||
| Flexural Yield Strength | 118 MPa | 17100 psi | ASTM D790 |
| Lendell Parapet EH-1000 PMMA, Extrusion |
|||
| Flexural Yield Strength | 118 MPa | 17100 psi | DIN 53455; ASTM D790 |
| Kolon KOPA® KN131 General Purpose Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
| Flexural Yield Strength | 118 MPa @Thickness 3.20 mm |
17100 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| LG Chemical LUMID GP3200B(W) PA66+MF20%, General Purpose Feature: Injection Molding, PA6+MF20%, General PurposeApplication: E&E (Rice Cooker Housing)Information provided by LG Chemical |
|||
| Flexural Yield Strength | 118 MPa | 17100 psi | DIN 53455; ASTM D790 |
| Kolon KOPA® KN333HS Heat Resistant Nylon 66 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstandin.. |
|||
| Flexural Yield Strength | 118 MPa @Thickness 3.20 mm |
17100 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| LG Chemical LUPOS GP2206F ABS+GF20%, Flame Retardant Feature: Injection Molding, ABS+GF20%, Flame RetardantApplication: Electric & Electronic (Housing, Components)CAS No. 9003-56-9, 9003-54-7, 65997-17-3, 88497-56-7 and 1309-64-4Information provided b.. |
|||
| Flexural Yield Strength | 118 MPa @Thickness 3.20 mm |
17100 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| LG Chemical Lupox® HI2100M PBT+GF10% Description: Injection Molding, PBT+GF10%, High ImpactApplication: IT/OA, E&E (Bobbin, Switch)CAS No. 65997-17-3, 155123-66-3 and 30965-26-5Information provided by LG Chemical |
|||
| Flexural Yield Strength | 118 MPa @Thickness 3.20 mm |
17100 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| LG Chemical LUPOY GN1000FA PC, Halogen Free, Flame Retardant, Transparency Description: Injection Molding, PC, Halogen Free Flame Retardant, TransparencyApplication: IT/OA, Electric & Electronic Housing and ComponentsCAS: 103598-77-2 and 181028-79-5Information provided by .. |
|||
| Flexural Yield Strength | 118 MPa @Thickness 3.20 mm |
17100 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| LG Chemical LUPOY GN2101FC PC+GF10%, Halogen Free, Flame Retardant, Heat Resistance Description: Injection Molding, PC+GF10%, Halogen Free Flame RetardanceApplication: IT/OA, Electric & Electronic Housing and ComponentsCAS: 103598-77-2 and 65997-17-3Information provided by LG Chemi.. |
|||
| Flexural Yield Strength | 118 MPa @Temperature 23.0 °C |
17100 psi @Temperature 73.4 °F |
ASTM D790 |
| IRPC Polimaxx Polene 120PC Styrene Acrylonitrile APPLICATIONS: INJECTION MOLDING, HOUSEHOLD PRODUCTS : SANITARY WARE, AUTOPART APPLICATION : LAMP ELECTRICAL APPLIANCES : ELECTRICAL FAN |
|||
| Flexural Yield Strength | 118 MPa @Temperature 23.0 °C |
17100 psi @Temperature 73.4 °F |
ASTM D790 |
| IRPC Polimaxx Polene 129PC Styrene Acrylonitrile APPLICATIONS: INJECTION MOLDING, HOUSEHOLD PRODUCTS : SANITARY WARE, AUTOPART APPLICATION : LAMP, ELECTRICAL APPLIANCES : ELECTRICAL FAN |
|||
| Flexural Yield Strength | 118 MPa @Temperature 23.0 °C |
17100 psi @Temperature 73.4 °F |
ASTM D790 |
| IRPC Polimaxx Polene 320PC Styrene Acrylonitrile APPLICATIONS: INJECTION MOLDING, HOUSEHOLD PRODUCTS : SANITARY WARE, AUTOPART APPLICATION : LAMP ELECTRICAL APPLIANCES : ELECTRICAL FAN |
|||
| Flexural Yield Strength | 118 MPa | 17100 psi | DIN 53455; ASTM D790 |
| Kolon KOPA® KN133G8ST Multi Reinforced Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
| Flexural Yield Strength | 118 MPa | 17100 psi | DIN 53455; ASTM D790 |
| Kolon KOPA® KN133HR Heat Resistant Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
| Flexural Yield Strength | 118 MPa @Thickness 3.20 mm |
17100 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| LG Chemical 80HF SAN, High Transparency, Heat Resistance, Chemical Resistance Feature: Injection Molding, SAN, High Transparency, Heat Resistance, Chemical ResistanceApplication: Refrigerator Sleeves, MiscellaneousCAS No. 9003-54-7Information provided by LG Chemical |
|||
| Flexural Yield Strength | 118 MPa @Thickness 6.40 mm |
17100 psi @Thickness 0.252 in |
30mm/min; ASTM D790 |
| LG Chemical LUPOL HM2300 PP+GF30% Description: Injection Molding, PP+GF30%, Good WeatherabilityApplication: Electrical, Electronic and Automotive Parts CAS: 9003-07-0 and 65997-17-3Information provided by LG Chemical |
|||
| Flexural Yield Strength | 118 MPa @Thickness 3.20 mm |
17100 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| LG Chemical LUPOY GP1000LG PC, Transparent Description: Injection Molding, PC, TransparencyApplication: IT/OA, Electric & Electronic Housing and ComponentsInformation provided by LG Chemical |
|||
| Flexural Yield Strength | 118 MPa | 17100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP WF002 PBT LNP* THERMOCOMP* WF002 is a compound based on PBT containing 10% Glass Fiber. |
|||
| Flexural Yield Strength | 118 MPa | 17100 psi | ASTM D790 |
| Shinkong Synthetic Fibers Shinite® P305G30 PP, 30% Glass Filled Information from Shinkong Synthetic Fibers Corp. |
|||
| Flexural Yield Strength | 118 MPa | 17100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Noryl GTX APS8740 PPE+PPS (Asia Pacific) Noryl* APS8740 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can be e.. |
|||
| Flexural Yield Strength | 118 MPa | 17100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL GTX EXNX0080 PPE+PPS Noryl APS* EXNX0080 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can.. |
|||
| Flexural Yield Strength | 118 MPa | 17100 psi | ASTM D790 |
| PlastxWorld CEVIAN® SKG20 20% GF ABS Glass fiber reinforced, heat resistant and flame retarded ABS.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by Plast.. |
|||
| Flexural Yield Strength | 118 MPa | 17100 psi | ASTM D790 |
| PlastxWorld CEVIAN® VGR20 20% GF ABS Glass fiber reinforced ABS.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
| Flexural Yield Strength | 118 MPa | 17100 psi | ASTM D790 |
| Cheng Yu Plastic N6C1 Nylon 6, 10% Mineral Reinforced |
|||
| Flexural Yield Strength | 118 MPa | 17100 psi | ASTM D790 |
| Cheng Yu Plastic PP238G3 Polypropylene, 30% Glass Fiber |
|||
| Flexural Yield Strength | 118 MPa | 17100 psi | ASTM D790 |
| Cheng Yu Plastic FRCV100 Flame Retardant Nylon 66, 10% Mineral Reinforced |
|||
| Flexural Yield Strength | 118 MPa @Thickness 6.40 mm |
17100 psi @Thickness 0.252 in |
1.3mm/min; ASTM D790 |
| LG Chemical LUPOL GP2300 PP+GF30% Description: Injection Molding, PP+GF30%, General PurposeApplication: Electrical & Electronic, Automotive PartsCAS: 9003-07-0 and 65997-17-3Information provided by LG Chemical |
|||